Polymer Property : Flexural Yield Strength = 16000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	48.3 - 110 MPa	7000 - 16000 psi	Average value: 84.8 MPa Grade Count:6
Overview of materials for Polyphenylene Ether, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Impact Grade". Each property range of values reported is minimum and maximum values..
Flexural Yield Strength	68.0 - 110 MPa	9860 - 16000 psi	Average value: 89.4 MPa Grade Count:101
Overview of materials for Polycarbonate, UV Stabilized This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, UV Stabilized". Each property range of values reported is minimum and maximum values of a..
Flexural Yield Strength	89.6 - 110 MPa	13000 - 16000 psi	Average value: 98.7 MPa Grade Count:8
Overview of materials for Polycarbonate, Aramid Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Aramid Fiber Reinforced". Each property range of values reported is minimum and maximum v..
Flexural Yield Strength	38.0 - 110 MPa @Temperature -40.0 - 80.0 °C	5510 - 16000 psi @Temperature -40.0 - 176 °F	Average value: 75.5 MPa Grade Count:1
Overview of materials for Nylon 6, 20% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are includ..
Flexural Yield Strength	76.0 - 110 MPa	11000 - 16000 psi	Average value: 93.0 MPa Grade Count:12
Overview of materials for Diallyl Phthalate (DAP), Cast, Mineral Filler This property data is a summary of similar materials in the MatWeb database for the category "Diallyl Phthalate (DAP), Cast, Mineral Filler". Each property range of values reported is minimum and ma..
Flexural Yield Strength	17.0 - 110 MPa	2470 - 16000 psi	Average value: 36.9 MPa Grade Count:38
Overview of materials for Polypropylene with 30% Calcium Carbonate (CaCO3) Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Calcium Carbonate (CaCO3) Filler". Each property range of values reported is mini..