Polymer Property : Flexural Yield Strength = 132 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	132 MPa	19100 psi	1.3 mm/min; ASTM D790
Ovation Polymers RIGITRON 10020 GF Polycarbonate, 20% Glass Reinforced PC - Glass reinforced (20 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared accor..
Flexural Yield Strength	132 MPa	19100 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Lubricomp DFP22H PC LNP* Lubricomp* DFP22H is a compound based on Polycarbonate containing Glass Fiber and PTFE. Characteristics of this grade are: Internally Lubricated and Healthcare.This data was supplied by SABIC..
Flexural Yield Strength	132 MPa	19200 psi	DIN 53455; ASTM D790
Kolon SPESIN® KP213G15HI Multi Reinforced PBT Resin (discontinued **) SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High hea..
Flexural Yield Strength	132 MPa	19100 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFL12 PC LNP* Lubricomp* DFL12 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated.
Flexural Yield Strength	132 MPa	19200 psi	DIN 53455; ASTM D790
Kolon KOPAÂ® KN3322VO Flame Retardant Nylon 66 KOPAÂ® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin..
Flexural Yield Strength	132 MPa	19100 psi	50 mm/min; ASTM D790
LG Chemical 95HC SAN Resin Heat and chemical resistance, Good mechanical properties, Excellent processability, Superior transparency, Good dimensional stability, Applications include make-up cases and other products requiring..
Flexural Yield Strength	132 MPa	19100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-LOY ZF3021 PPE+PS (Europe-Africa-Middle East) LNP* STAT-LOY* ZF3021 is a compound based on PPE + PS Blend resin containing Glass Fiber. Added features include Antistatic, Flame Retardant.
Flexural Yield Strength	132 MPa	19100 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp DFZ22E PC LNP* Thermocomp* DFZ22E is a compound based on Polycarbonate with Glass and Milled Fiber. Characteristics of this products is Easy Molding.This data was supplied by SABIC-IP for the Americas region..
Flexural Yield Strength	132 MPa	19200 psi	ASTM D790
Samyang TribitÂ® 1500GN15 Polybutylene Terephthalate, 15% Glass Reinforced, Flame Retardant Characteristics:G/F reinforcedFlame retardantHeat and Impact resistantApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A..
Flexural Yield Strength	132 MPa	19100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP WFB33E PBT (Europe-Africa-Middle East) LNP THERMOCOMP WFB33E is a compound based on Polybutylene Terephalate resin containing Glass Fiber and Glass Bead. Added features include Easy Molding.
Flexural Yield Strength	132 MPa	19200 psi	ASTM D790
PlastxWorld CEVIAN® B5524 20% GF PBT/ABS Alloy Glass fiber reinforced and flame retarded PBT/ABS alloy.Information provided by PlastxWorld Inc.
Flexural Yield Strength	132 MPa	19100 psi	Neat Resin; ASTM D790
Hexcel® HexFlow® RTM 6 180°C Epoxy System for Resin Transfer Molding Monocomponent System HexFlow® RTM 6 is a monocomponent resin already degassed, specifically developed to fulfill the requirements of the aerospace and space industries in advanced resin transfer moulding (RTM) process...
Flexural Yield Strength	132 MPa	19200 psi	ASTM D790
Cheng Yu Plastic N6CV3 Flame Retardant Nylon 6, 30% Mineral Reinforced
Flexural Yield Strength	132 MPa	19200 psi	ASTM D790
Cheng Yu Plastic NG1100S Nylon 66, 10% Glass Fiber Reinforced
Flexural Yield Strength	132 MPa	19200 psi	ASTM D790
Cheng Yu Plastic FR200GV10 Flame Retardant Nylon 66, 10% Glass Fiber
Flexural Yield Strength	132 - 269 MPa	19100 - 39000 psi	Average value: 209 MPa Grade Count:8
Overview of materials for Polyethylene Terephthalate (PET), 40% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 40% Glass Reinforced". Specific grades with glass content between 35% ..
Flexural Yield Strength	132 MPa	19100 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP GFL36 PSU (Europe-Africa-Middle East) LNP* Lubricomp* GFL36 is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated.