Polymer Property : Flexural Yield Strength = 130 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	130 MPa	18900 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Opnyl OP66GF13 Nylon 66, 13% Glass Reinforced Nylon 66 - Glass reinforced (13 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared..
Flexural Yield Strength	130 MPa	18900 psi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Uttap SF 600 Polyethersulfone Polyether Sulfone Resin-Medium Viscosity, unreinforced standard grade for Easy Injection Molding.Information provided by Ovation Polymers
Flexural Yield Strength	130 MPa	18900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP COLORCOMP J1000Z PES (Europe-Africa-Middle East) LNP* COLORCOMP* is a compound based on Polyethersulfone resin. Added features include: High Viscosity
Flexural Yield Strength	130 MPa @Temperature 90.0 °C	18900 psi @Temperature 194 °F	ISO 178, ASTM D790
Nilit Nilamid A G5 FR C4 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Halogens) Description: Nilamid A G5 FR C4 combines excellent mechanical performance with flame retardancy. The halogenated flame retardant system used in this product allows a wide range of colors. This produ..
Flexural Yield Strength	130 MPa	18900 psi	ISO 178, ASTM D790
Nilit Nilamid B G4 FR HF 20% Glass Fiber Reinforced, Flame Retardant PA6 Description: Nilamid B G4 FR HF is a NYLON 6 based flame retardant compound that does not contain any halogen or red phosphorous. It has a good overall mechanical performance, has an excellent price..
Flexural Yield Strength	130 MPa	18900 psi	DIN 53 452
Albis Plastics Tedur® L 9561 PPS, 60% Glass Fiber/Mineral (discontinued **) High Gloss, Highest Surface Finish, Metallization w/o Base Coating. Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Various High Temperature ReflectorsProcessing: Inje..
Flexural Yield Strength	130 - 388.175 MPa @Temperature -40.0 - 121 °C	18900 - 56300.1 psi @Temperature -40.0 - 250 °F	Average value: 225 MPa Grade Count:8
Overview of materials for Nylon 66, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. ..
Flexural Yield Strength	130 MPa	18900 psi	ASTM Data
BASF Capron® 1202CQ Nylon 6 (Dry) (discontinued **) Capron 1202CQ is a blended low viscosity, polyamide 6 injection molding homopolymer, possessing a modified crystalline structure for increased property performance and faster cycles. It is also ava..
Flexural Yield Strength	130 MPa	18900 psi	ASTM Data
BASF Capron® 5202 HS Blend Nylon 66 (Dry) (discontinued **) Capron 5202 HS Blend is a blended, unfilled, heat stabilized, nylon 6,6, injection molding compound. It is also available in natural and pigmented versions. It combines strength and stiffness as wel..
Flexural Yield Strength	130 MPa	18900 psi	ASTM D790
Lucky CF-920 Acrylic May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent chemical resistance and coloring capability.
Flexural Yield Strength	130 MPa	18900 psi	ASTM D790
Lucky EG-920 Acrylic, Extrusion Grade Special extrusion grade with excellent stress cracking resistance, intended mainly for exterior applications. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, hi..
Flexural Yield Strength	130 MPa	18900 psi	ASTM D790
Lucky EG-930 Acrylic, Injection Grade Injection molding grade. May be UV stabilized. General Lucky PMMA qualities: Transparent/elegant appearance, high heat and weather resistance, excellent chemical resistance and coloring capability..
Flexural Yield Strength	130 MPa	18900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP UAL23AS PPA (Europe-Africa-Middle East) LNP* LUBRICOMP* UAL23AS is a compound based on Polyphthalamide resin containing Aramide Fiber, PTFE. Added features include : Internally Lubricated, Heat Stabilized.
Flexural Yield Strength	130 MPa	18900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 4002 PEI PTFE filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL 94 V0 and 5VA listing in recognized colors.
Flexural Yield Strength	130 MPa	18900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 9075 PEI (Europe-Africa-Middle East) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution.
Flexural Yield Strength	130 MPa	18900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM LTX300A PEI Copolymer High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors.
Flexural Yield Strength	130 MPa	18900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem LTX300A PEI Copolymer (Europe-Africa-Middle East) High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle East..
Flexural Yield Strength	130 MPa	18900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 4012 PBT (Europe-Africa-Middle East) VALOX 4012 is a 10% high strength glass fibre reinforced PBT injection moulding resin with improved mechanical properties. Applications: connectors.
Flexural Yield Strength	130 MPa	18900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® DR48 PBT (Europe-Africa-Middle East) VALOX DR48 is a 17% glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromoto..
Flexural Yield Strength	130 MPa	18900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® ENH4530 PBT (Europe-Africa-Middle East) 15% GF PBT, Non-Brominated & Non-Chlorinated Flame retardant
Flexural Yield Strength	130 MPa	18900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP WFB62 PBT LNP* THERMOCOMP* WFB62 is a compound based on PBT resin containing 10% Glass Fiber, 10% Glass Bead. Added feature of this grade is: Low Warpage.
Flexural Yield Strength	130 MPa	18900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL PKN4752 PPE+PS (Europe-Africa-Middle East) NORYL PKN4752 is a translucent, high heat PPO+PS extrusion grade for dilution with polystyrene resin. It is suitable for (microwavable) food packaging and is compliant with US and European food cont..
Flexural Yield Strength	130 MPa	18900 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM LTX300A PEI Copolymer (Asia Pacific) High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors.
Flexural Yield Strength	130 MPa	18900 psi	ISO 178
Wellman Wellamid® MR410 42H-N 40% Mineral Reinforced Nylon 6, Heat Stabilized Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co..
Flexural Yield Strength	130 MPa	18900 psi	ISO 178-93
Wellman Wellpet® MRGF101-GY1 PET, 29% Mineral/Glass Fiber Reinforced Typical data obtained from injection molded test bars, tested dry as molded at 73°F (23°C). Information provided by Wellman, Inc. Engineering Resins Division.
Flexural Yield Strength	130 - 150 MPa	18900 - 21800 psi	ASTM D790
Chang Chun Plastic PBT3015 15% Glass Fiber Enforced PBT Information provided by Dowell Trading Company Ltd.
Flexural Yield Strength	130 MPa	18900 psi	ASTM Data
BASF Capron® 8360 HS 34% Mineral-Filled Nylon 6 (Dry) (discontinued **) Capron 8360 HS is a heat stabilized 34% mineral reinforced nylon 6 injection molding resin possessing a high level of toughness and ductility combined with excellent processability and surface aesth..
Flexural Yield Strength	130 MPa	18900 psi	ASTM D790
E-Polymers Tekaloy® T80G20 , 20% Glass Fiber Reinforced PBT/ABS Alloy 20% Glass Fiber reinforcedInformation provided by E-Polymers Co. Ltd.
Flexural Yield Strength	130 MPa	18900 psi	ASTM D790
Chevron Phillips Ryton® PR09-60 Polyphenylene Sulfide Compound, Annealed 2 hours at 200°C (discontinued **)&l Polyphenylene Sulfide CompoundRyton® PR09-60 Annealed 2 hours at 200°C is pelletized unfilled high molecular weight polyphenylene sulfide resin suitable for extrusion or injection molding.Comments..
Flexural Yield Strength	130 - 265 MPa	18900 - 38400 psi	Average value: 182 MPa Grade Count:42
Overview of materials for Polyethylene Terephthalate (PET), Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Glass/Mineral Reinforced". Each property range of values reported is m..