Polymer Property : Flexural Yield Strength = 113 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	113 MPa	16400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycoloy® MC5220 PC+ABS (Europe-Africa-Middle East) CYCOLOY MC5220 is a 20% glass reinforced PC+ABS blend for injection moulding purposes.
Flexural Yield Strength	113 MPa	16400 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Lexan® EX7631T PC EX7631T is a high UVA content homopolymer polycarbonate product intended for use as a cap layer for polycarbonate sheet extrusion.
Flexural Yield Strength	113 - 200 MPa	16400 - 29000 psi	Average value: 160 MPa Grade Count:16
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler". Specific grades with glass content between 15%..
Flexural Yield Strength	113 MPa @Thickness 6.40 mm	16400 psi @Thickness 0.252 in	2.8mm/min; ASTM D790
LG Chemical LUMID GN1001BF PA66, Halogen Free Flame Retardant Feature: Injection Molding, PA66, Halogen Free Flame RetardantApplication: ConnectorsCAS No. 32131-17-2, 25038-54-4 and 37640-57-6Information provided by LG Chemical
Flexural Yield Strength	113 MPa @Thickness 3.20 mm	16400 psi @Thickness 0.126 in	2.8mm/min; ASTM D790
LG Chemical LUMID GP1000B(W) PA66, General Purpose, Low Viscosity Feature: Injection Molding, PA66, General Purpose, Low ViscosityApplication: Buckles, Chair NobCAS No. 32131-17-2Information provided by LG Chemical
Flexural Yield Strength	113 MPa @Thickness 3.20 mm	16400 psi @Thickness 0.126 in	1.3mm/min; ASTM D790
LG Chemical LUMID GP3200A(W) PA6+MF20%, General Purpose Feature: Injection Molding, PA6+MF23%, High ImpactPA6+MF15%, General PurposeApplication: E&E (Rice Cooer Housing)CAS No. 25038-54-4 and 9010-79-1Information provided by LG Chemical
Flexural Yield Strength	113 MPa @Thickness 3.20 mm	16400 psi @Thickness 0.126 in	10mm/min; ASTM D790
LG Chemical LUPOY GP5056F PC/ABS+GF5%, Flame Retardance Description: Injection Molding, PC/ABS+GF5%, Flame Retardance, General PurposeApplication: IT/OA (Housing)CAS: 103598-77-2, 9003-56-9, 68928-70-1, 1309-64-4 and 65997-17-3Information provided by LG ..
Flexural Yield Strength	113 MPa	16400 psi	50 mm/min; ASTM D790
LG Chemical 81HF SAN Resin High flow, Heat and chemical resistance, Good mechanical properties, Excellent processability, Superior transparency, Good dimensional stability, Applications include food receptacles, disposable li..
Flexural Yield Strength	113 MPa	16400 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL PX9406P PPE NORYL* PX9406P resin is an FR (non-halogenated) grade potentially suitable for a variety of electronics applications. RTI (impact) = 105 C. F1 listed in BK color.
Flexural Yield Strength	113 MPa	16400 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 4000 PEI Glass fiber, PTFE, and Graphite filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 listing.
Flexural Yield Strength	113 MPa	16400 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 4000 PEI (Asia Pacific) Glass fiber, PTFE, and Graphite filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 listing.
Flexural Yield Strength	113 MPa	16400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermocomp GX061104 PSU (Europe-Africa-Middle East) LNP* COLORCOMP* GX061104 is a compound based on Polysulfone resin.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength	113 MPa	16400 psi	ASTM D790
Samyang TramidÂ® 210P Polyamide, High Productivity Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.210P is a high productivity grade.Applications:ConnectorsCable tiesHarness clipsT..
Flexural Yield Strength	113 MPa	16400 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GTX GTX975 PPE+PA NORYL GTX975 is a 18% mineral filled material especially designed for in- or on-line painted exterior automotive trim part, e.g. tankflaps and corner panels. This material combines high stiffness an..
Flexural Yield Strength	113 MPa	16400 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GTX GTX975 PPE+PA (Asia Pacific) NORYL GTX975 is a 18% mineral filled material especially designed for in- or on-line painted exterior automotive trim part, e.g. tankflaps and corner panels. This material combines high stiffness an..
Flexural Yield Strength	113 MPa	16400 psi	2.6 mm/min, 100 mm span; ASTM D 790
SABIC Innovative Plastics Noryl 534 PPE+PS High heat, unreinforced.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	113 MPa	16400 psi	ASTM D790
PlastxWorld CEVIAN® SERG3 30% GF ABS Glass fiber reinforced and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc.
Flexural Yield Strength	113 MPa	16400 psi	ASTM D790
Cheng Yu Plastic N6CV1 Flame Retardant Nylon 6, 10% Mineral Reinforced
Flexural Yield Strength	113 MPa	16400 psi	2 mm/min; ISO 178
Eurostar Starglas GX061104 PSU Starglas GX061104 is a PSU resin (also known as Starglas PSU A ¾)Information provided by Eurostar.
Flexural Yield Strength	113 MPa @Thickness 6.40 mm	16400 psi @Thickness 0.252 in	5 mm/min; ASTM D790
Bhansali Engineering Santron IMS 2006 SAN Resin Very High Rigidity Clear SANInformation provided by Bhansali
Flexural Yield Strength	113 MPa @Thickness 6.40 mm	16400 psi @Thickness 0.252 in	5 mm/min; ASTM D790
Bhansali Engineering Santron IMS 2006 SAN Resin Very High Rigidity Clear SANInformation provided by Bhansali