Polymer Property : Film Tensile Strength at Break, TD = 6240 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	43.0 MPa	6240 psi	ASTM D882
NOVA Chemicals Surpass® HPs900-C Octene sLLDPE Film Resin Features: Easy processabilityExceptional clarity and glossLow gelExcellent seal properties Applications: High clarity applications Lamination film Coextruded sealant layerHigh toughness filmInformat..
Film Tensile Strength at Break, TD	43.0 MPa	6240 psi
Reliance Industries LLDPE film - 1 MI O-LLDPE films Information provided by Reliance Industries
Film Tensile Strength at Break, TD	43.0 MPa	6240 psi	2 in per min; ASTM D882
Chevron Phillips Marlex® D252/257 Linear Low Density Polyethylene Film Resin (discontinued **) Low Density, Linear Polyethylene Film ResinCustomer Benefits: This unique broad molecular weight distribution resin has a wide processing window and produces film with an excellent combination of to..
Film Tensile Strength at Break, TD	43.0 MPa	6240 psi	ASTM D882
Chevron Phillips HiD® 9632 HDPE Blown Film Resin (discontinued **) Characteristics: Copolymerization Enhances Film Toughness, Excellent Film Drawdown Ideally Suited for Thin Films Production, Lower Melt Index (Higher Molecular Weight) Results in Increased Film Stre..
Film Tensile Strength at Break, TD	43.0 MPa	6240 psi	ASTM D882
Chevron Phillips HiD® 9650 HDPE Blown Film Resin (discontinued **) Resin Type: Linear Polyethylene CopolymerCharacteristics: Copolymerization Enhances Film Toughness, Excellent Film Drawdown, Unique Molecular Architecture Gives Moisture Barrier Properties Typical o..
Film Tensile Strength at Break, TD	43.0 MPa	6240 psi	ASTM D882-02
Ipiranga Petrochem LB 0120 BPS LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Film Tensile Strength at Break, TD	43.0 MPa	6240 psi	ASTM D882-02
Ipiranga Petrochem LBH 0120 BPS LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Film Tensile Strength at Break, TD	<= 43.0 MPa	<= 6240 psi	ISO 527-1.3
Iran Petrochemical (PCC) MF3313 High Density Polyethylene MF3313 is a high molecular weight high density polyethylene . Applications: extrusion, film, blown, bags, and density modifies.Information provided by Iran Petrochemical Commercial Co.
Film Tensile Strength at Break, TD	43.0 MPa	6240 psi
UBE 5033B Air Blown Nylon 6/66 Film Specialties: Standard nylon 6/66Medium shrink, Low slipApplications: Best for Middle layer usageProcessing: Top web (Air blown)Thermoforming (T-die)Information provided by UBE.
Film Tensile Strength at Break, TD	43.0 MPa	6240 psi
UBE 7024B Five Layer Film Specialties: High transparencyGood thermoform-abilityLow W.V.T.R High shrink-abilityLower extrusion temperatureProcessing: Best match for co-extrusion with EVOH resins.Typical Applications: Cereal ..
Film Tensile Strength at Break, TD	43.0 MPa	6240 psi	Blown Film at 1 mil; ASTM D-882
Chevron Phillips MarFlex® 7105D Polyethylene; LLDPE Hexene linear low density polyethylene. This LLDPE is tailored for blown film applications that require: High strengthGood drawdownGood processabilityUse alone or in blends with LDPE or HDPE Appl..