Polymer Property : Film Tensile Strength at Break, TD = 37.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	37.0 MPa	5370 psi	ASTM D882
SABIC F04660 High Density Polyethylene for Blown Film Applications Product Description: F04660 is a homopolymer HDPE film grade with excellent processability and high stiffness. It has good moisture barrier properties and can be blended with LDPE and LLDPE to imp..
Film Tensile Strength at Break, TD	37.0 MPa	5370 psi	ASTM D882
NOVA Chemicals Sclair® 12J1 Octene LLDPE Film Resin (discontinued **) Film Properties. Features: Low gel, high clarity.Applications: Overwrap, lamination.Data provided by the manufacturer.
Film Tensile Strength at Break, TD	37.0 MPa	5370 psi	ASTM D882
ExxonMobil Escorene® LL-1117 LLDPE Film/Sandwich Bag Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.An LLDPE blown film resin. Films made from LL-1117 have very good tensile properties and toughness. This resin's good strength and drawability all..
Film Tensile Strength at Break, TD	37.0 MPa	5370 psi	ASTM D882
ExxonMobil Escorene® LD 767.MJ Blown Film Resin (discontinued **) Escorene Ultra LD 767.MJ is a low gel 29.5% vinyl acetate copolymer designed for film and compounding applications.Information provided by ExxonMobil Chemical
Film Tensile Strength at Break, TD	37.0 MPa	5370 psi	ASTM D882
NOVA Chemicals Sclair® 14A Butene MDPE Film Resin (discontinued **) Film Properties. Features: Low gel, strength and toughness, broad MW distribution.Applications: Co-extrusion, blending.Data provided by the manufacturer.
Film Tensile Strength at Break, TD	37.0 MPa	5370 psi	ASTM D882-02
Ipiranga Petrochem LB 0120 BP LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Film Tensile Strength at Break, TD	37.0 MPa	5370 psi	ASTM D882-02
Ipiranga Petrochem LBH 0117 LLDP IPQ produces Linear Low Density Polyethylene (LLDPE) for use by plastics molding industry segments that employ extrusion processes in the manufacturing of films destined for producing bobbins and ba..
Film Tensile Strength at Break, TD	37.0 MPa	5370 psi	ASTM D882
SCG Chemicals EL-Leneâ„¢ F15 High Density Polyethylene Film Key Characteristics:High productivityHigh tensile strengthHigh dart impactHigh stiffnessLow gel contentGood moisture barrierExcellent printabilityRecommended Applications:High speed processingWide l..
Film Tensile Strength at Break, TD	37.0 MPa	5370 psi	ISO 527-3
Total EVA 1005 VN 35 Ethylene Vinyl Acetate Copolymer - Blown Film EVA 1005 VN 35 is made by a high pressure tubular process. Grade for flexible films, with high transparency and outstanding mechanical properties. Contains NO antioxidant.Information provided by T..
Film Tensile Strength at Break, TD	37.0 MPa	5370 psi	ASTM D882
Braskem LH 0820/30 AF LLDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Lamination; heavy duty bags; blends with LDPE and HDPE; valvulated heavy duty bags. Information provided by Braske..