Polymer Property : Film Tensile Strength at Break, TD = 33.1 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Break, TD 33.1 MPa
4800 psi
1 mil; ASTM D882
NOVA Chemicals Sclair® FP026-F Octene LLDPE Film Resin
Features: Moderate toughness and strengthGood stiffnessEasy processabilityExcellent seal properties Applications: Heavy duty shipping sacks requiring moderate toughness and high stiffnessIndustrial ..
Film Tensile Strength at Break, TD 33.1 MPa
4800 psi
ASTM D882
Chevron Phillips MarFlex® 7120 LLDPE Blown & Cast Film Resin  (discontinued **)
Resin Type: linear low density polyethylene, hexene copolymerCharacteristics: good stiffness at thin gauges, good drawdown, excellent processability, can use straight or in blends with LDPE or HDPE,..
Film Tensile Strength at Break, TD 33.1 MPa
4800 psi
ASTM D882
Chevron Phillips MarFlex® 7120S LLDPE Blown & Cast Film Resin  (discontinued **)
Resin Type: linear low density polyethylene, hexene copolymer with enhanced stabilization packageCharacteristics: good stiffness at thin gauges, good drawdown, excellent processability, can use stra..
Film Tensile Strength at Break, TD 33.1 MPa
4800 psi
ASTM D882
Westlake LF2040 Hexene Linear Low Density Polyethylene
Westlake LF2040 is a hexene LLDPE with excellent physical properties and heat sealing characteristics, which allow for down-gauging and blending with other materials. Typical applications include s..
Film Tensile Strength at Break, TD 33.1 MPa
4800 psi
50 µm (2 mil) film; ASTM D882
DuPont Nucrel® 1202HC Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film
11.5 wt% Methacrylic Acid.Nucrel® 1202HC (High-Clarity) is an ethylene-methacrylic acid copolymer resin available for use in conventional blown and cast film extrusion and coextrusion equipment des..
Film Tensile Strength at Break, TD 33.1 MPa
4800 psi
ASTM D882, A
Total Lumicene® mPE M 2710 EP Metallocene Polyethylene, Film
Metallocene Medium Density Film ResinCharacteristics:Outstanding clarity and glossExcellent bubble stabilityExcellent tear strengthHigh puncture resistanceGood stiffnessExcellent heat sealing proper..
Film Tensile Strength at Break, TD 33.1 MPa

@Thickness 0.0254 mm
4800 psi

@Thickness 0.00100 in
ASTM D882A
Total Lumicene® mPE M 3410 EP HDPE Film
Outstanding clarity and gloss; excellent bubble stability; excellent tear strength; high puncture resistance; good stiffness; excellent heat sealing properties; excellent compatibility with LDPE and..
Film Tensile Strength at Break, TD 33.1 MPa
4800 psi
ASTM D882
Chevron Phillips MarFlex® 7120B LLDPE Blown & Cast Film Resin
Resin Type: linear low density polyethylene, hexene copolymerCharacteristics: good stiffness at thin gauges, good drawdown, excellent processability, can use straight or in blends with LDPE or HDPE,..
Film Tensile Strength at Break, TD 33.1 MPa
4800 psi
ASTM D882
Dow INTEGRAL™ 932 High Heat Multilayer Adhesive Film
INTEGRAL 925 High Heat Adhesive Film is a heat-activated, thermally stable adhesive film for automotive applications capable of bonding to urethane foam-baked fabrics, paper, fiberglass, non-wovens,..
Film Tensile Strength at Break, TD 33.1 - 40.0 MPa
4800 - 5800 psi
3M 6145 Kraft Light Duty Reinforced Water Activated Tape
3M™ Light Duty Reinforced Water Activated Tape 6145 is used for box sealing and other packaging applications. This product has a fiberglass reinforced paper backing and a high tack water-activated ..
Film Tensile Strength at Break, TD 33.1 MPa
4800 psi
ASTM D882
DuPont™ Surlyn® 1802 Sodium Ionomer Resin for Blown/Cast Film and Extrusion Coating
Surlyn® 1802 is an ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment and extrusion coating and coextrusion coating equipment designed to proces..