Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	207 MPa	30000 psi	20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor® 75 AB-X OPP Film Product Description: Bicor AB-X is a two-side coated, sealable OPP film designed for general use in many applications, including overwrap, horizontal and vertical packaging. This film is suitable as..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor® 85 AXT OPP Film Product Description: Bicor ASB-X is a two side coated, sealable OPP film delivering an advanced level of moisture and oxygen battier protection. This film is designed for use in (unsupported and sur..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 18 MAT OPP Film Product Description: Bicor MAT is a one-side matte finish, one-side treated, non-heat sealable OPP film designed for use as the outer web of a lamination. MAT is also an excellent matte finish slip ..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Melinex® 514P Polyester Film This high clarity film has one side hydrophilic pretreated to promote adhesion to many solvent coatings formulations, while the opposite side is pretreated to provide antistatic protection.Informati..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Melinex® 561 Polyester Film Melinex® 561 is a high clarity polyester film which is pretreated on both sides to promote adhesion to many industrial coatings and inks. Melinex® 561 is suitable for applications which require a ..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Melinex® 965 Polyester Film, 500 Gauge Melinex® 965 is a slightly hazy film with internal UV blocker. It is pretreated on one surface to promote adhesion to many solvent systems. It has a superb web handleability.Information provided by..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Melinex® 966 Polyester Film, 700 Gauge Melinex® 966 is a slightly hazy film with internal UV blocker. It is pretreated on one surface to promote adhesion to many solvent systems. It has a superb web handleability.Information provided by..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® EL Polyester Film, 500 Gauge Mylar® EL films, typically 48 through 500 gauge are strong, tough, general -purpose films for electrical/electronic uses. Heavier gauges of Mylar® EL films are similar to Mylar® MO films. Availab..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® EL21 Polyester Film, 750 Gauge Mylar® EL21 polyester films are flexible strong and durable films with an unusual balance of properties, making them suitable for a variety of industrial applications. The excellent dielectric stre..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 1000 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 142 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 400 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 500 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 650 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® MDA Polyester Film, 750 Gauge Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® MO Polyester Film, 500 Gauge Product Description: Mylar® MO polyester film has excellent electrical properties. This film offer exceptional cut-through resistance, low shrinkage, low moisture absorption, and high thermal durab..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® S2 Polyester Film, 750 Gauge Mylar® S2 is a slightly hazy film designed for use in the production of drumheads. It has low haze, excellent impact resistance, and balanced physical properties, resulting in consistent tonal qual..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor® 70 HBS-2 OPP Film Product Description: Bicor HBS-2 is a one-side sealable, one-side high barrier PVdC-coated OPP film designed for use as the inside sealant web in high-barrier laminations.Availability: Latin America..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Melinex® 943 Polyester Film Melinex® 943 is a super clear film with internal UV blocker. It is pretreated on one surface to promote adhesion to many solvent systems.Information provided by DuPont.
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® A Polyester Film, 500 Gauge Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, ..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® A Polyester Film, 750 Gauge Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, ..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 92 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® MDA Polyester Film, 400 Gauge Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® MDA Polyester Film, 500 Gauge Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® MO21 Polyester Film, 750 Gauge Product Description: Mylar® type MO21 films are strong, heavy gauge films that have excellent electrical properties. These films offer exceptional cut-through resistance, low shrinkage, low moistur..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® WC Polyester Film, 500 Gauge Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling char..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 200 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® LJP Polyester Film, 300 Gauge Mylar® LJP is an industrial grade very clear film that is available with adhesion promoting coatings and slip coatings. For higher quality end-uses (especially for surface requirements) consider us..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® S2 Polyester Film, 1000 Gauge Mylar® S2 is a slightly hazy film designed for use in the production of drumheads. It has low haze, excellent impact resistance, and balanced physical properties, resulting in consistent tonal qual..
Film Tensile Strength at Break, TD	207 MPa	30000 psi	ASTM D882A
DuPont Teijin Films Mylar® WC Polyester Film, 400 Gauge Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling char..