Polymer Property : Film Tensile Strength at Break, TD = 290 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	290 MPa	42100 psi	ASTM D882
Eastman Eastman Embrace Copolyester for Shrink Film Applications:Flexible packagingIV containersLabels to fit high contour containersShrink packagingWrap around designKey Attributes:Excellent clarityExcellent printabilityGood chemical resistanceGood ..
Film Tensile Strength at Break, TD	290 MPa	42000 psi	ExxonMobil Method
ExxonMobil Bicor® 100 CSR-2 OPP Film Product Description: Bicor CSR-2 is a one-side treated OPP film designed for cold seal release, either unsupported or as the outer web of a lamination.Availability: Latin America, North America and ..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 15MB400 OPP Film Product Description: Bicor 15MB400 is one side treated, sealable coextruded OPP film. It is designed for use in laminations.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Ou..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 18MB090 OPP Film Product Description: Biaxially oriented polypropylene film metallizable on one side, with a slip controlled broad seal range surface on the other side. Once metalized, film designed to be used in la..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 20MB080 OPP Film Product Description: Bicor 20NB080 is a biaxially oriented polypropylene film metallizable on one side, with a heat sealable surface on the other side. Designed to be used after metallization as a s..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 20MB666 OPP Film Product Description: Bicor 20MB666 is a biaxially oriented transparent polypropylene film acrylic coated two sides. It provides outstanding performance on all packaging machines and is mainly propos..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 20MB668 OPP Film Product Description: Bicor 20MB668 is a high speed transparent, biaxially oriented polypropylene film, coated one side acrylic, one side very low temperature seal (VLTS) coating. VLTS coating provid..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 21MB777 OPP Film Product Description: Bicor 21MB777 is a high gas barrier, biaxially oriented transparent PP film coated one side PVdC, one side acrylic. This film provides outstanding performance on all packaging m..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 25MB400 OPP Film Product Description: Heat seal coextruded biaxially oriented polypropylene film that can be used on a wide range of packaging machines. 25MB400 can be either used as mono material or in laminated st..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 25MB666 OPP Film Product Description: A Biaxially oriented transparent polypropylene film, acrylic coated two sides. It provides outstanding performance on all packaging machines.Availability: Africa & Middle East, ..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 25MB668 OPP Film Product Description: A high speed transparent, biaxially oriented polypropylene film, coated one side acrylic, one side very low seal temperature (VLTS) coating. VLTS coating provides excellent perf..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 25MBT666 OPP Film Product Description: Biaxially oriented polypropylene film, acrylic coated two sides. This film is specifically suitable for unsupported overwrapping offering unique aspect and cost reduction advant..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 26MB777 OPP Film Product Description: A high gas barrier, biaxially oriented transparent polypropylene film, coated on one side PVdC, one side acrylic. This film provides outstanding performance on all packaging mac..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 29MB080 OPP Film Product Description: A biaxially oriented polypropylene film metallizable on one side, with a heat sealable surface on the other side. Designed to be used after metallization as a single web in HFFS..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 30MB400 OPP Film Product Description: A heat sealable coextruded biaxially oriented polypropylene film that can be used on a wide range of packaging machines. 30MB400 can be either used as mono material or in lamina..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 30MB668 OPP Film Product Description: A high speed transparent, biaxially oriented polypropylene film, coated one side very low temperature seal (VLTS) coating. VLTS coating provides excellent performances on high s..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 32MB777 OPP Film Product Description: A high gas barrier, biaxially oriented transparent polypropylene film, coated one side PVdC, one side acrylic. This film provides outstanding performance on all packaging machin..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 17LL222 OPP Film Product Description: An uncoated biaxially oriented, transparent polypropylene film designed for overlamination in labeling applications where high gloss and high transparency are required.Availabil..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 18MM383 OPP Film Product Description: A biaxially oriented very high barrier metalized polypropylene film. This film offers an outstanding moisture barrier and a broad seal range surface on the other side. This film..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 18MM388 OPP Film Product Description: A metallized biaxially oriented polypropylene film, metalized on one side with a broad seal range surface on the other side. This film is designed for high barrier performance p..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 18MM488 OPP Film Product Description: A metalized biaxially oriented polypropylene film, metalized on one side. MM488 is typically used in laminates as the inner web for VFFS and HFFS applications. Due to its slip c..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Metallyte™ 20MM480 OPP Film Product Description: A metalized biaxially oriented polypropylene film, metalized on one side, heat sealable on the other side. It is typically used in lamination with other substrates on HFFS and V..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	ASTM D882A
DuPont Teijin Films Mylar® 813 Polyester Packaging Film, 48 Gauge Data provided by DuPont Packaging Polymers.Melinex® 813 is a polyester film, pretreated on one side to provide excellent adhesion to a wide range of both solvent- and water-based inks. Melinex® 8..
Film Tensile Strength at Break, TD	290 MPa	42000 psi	ASTM D882A
DuPont Teijin Films Mylar® 814 Polyester Film, 48 Gauge Mylar® 814 is a one-side pretreated polyester film which was designed for UV cure inks and also works well for EB cure overlaquers. General Product Info: Mylar® 814 is designed to provide excellen..
Film Tensile Strength at Break, TD	290 MPa	42000 psi	ASTM D882A
DuPont Teijin Films Mylar® X842 Polyester Film, 48 Gauge Mylar® X842 is a clear polyester film that has been chemically treated on both sides for the packaging converting market. One side is chemically treated for metal adhesion. The other side is chemic..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 17MB400 OPP Film Product Description: Bicor 17MB400 is one side treated, sealable coextruded OPP film. It is designed for use in laminations.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Ou..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 30MBT666 OPP Film Product Description: A biaxially oriented transparent polypropylene film, acrylic coated two sides. This film is specifically suitable for unsupported overwrapping, offering unique aspect and cost r..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	ASTM D882A
DuPont Teijin Films Mylar® 822 Polyester Packaging Film, 48 Gauge Data provided by DuPont Packaging Polymers.Melinex® 822 is a polyester film that has been chemically pretreated on one side. It is designed for printing and extruded polyethylene adhesion. Melinex..
Film Tensile Strength at Break, TD	290 MPa	42000 psi	ASTM D882A
DuPont Teijin Films Mylar® M813 Polyester Film, 48 Gauge Mylar® M813 is a clear, pretreated base film with high gloss, low haze, and excellent processability. It is a one side pre-treated polyester designed for improved ink adhesion and may be suitable f..
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Bicor™ 20MBT666 OPP Film Product Description: Bicor 20MBT666 is a biaxially oriented transparent polypropylene film acrylic coated two sides. This film is specifically suitable for unprinted overwrapping, offering unique as..