Polymer Property : Film Tensile Strength at Break, TD = 28.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ISO 527-3
Polimeri Europa Greenflex® FF 35 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion
Greenflex FF 35 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. The resin shows good strechability and sealability.Main Applications: Greenflex FF 35 is suitable for flexibl..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ISO 527-3
Polimeri Europa Riblene® FC 40 Low Density Polyethylene - Blown Film Extrusion
Riblene FC 40 is a high molecular weight low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FC 40 is characterized by a high melt strength leading to a good bubble stability..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D882
NOVA Chemicals Novapol® TF-Y822-BP Hexene LLDPE Film Resin
Film Properties. Features: Good stiffness and machinability, exceptional toughness.Applications: Industrial packaging, high strength liners.Data provided by the manufacturer.
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D 882
NOVA Chemicals Surpass® FPs225-A Octene Copolymer sLLDPE Film Resin
FPs225-A complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food, without ..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D882
ExxonMobil Escorene® LL-1042 LLDPE Packaging Film Resin, Clarity  (discontinued **)
Data provided by the manufacturer, Exxon Chemical.An LLDPE blown clarity film resin. Films made from LL-1042 have very good tensile properties and toughness in addition to good clarity The good st..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D882
Iran Petrochemical (PCC) Arak 1209AA LLDPE  (discontinued **)
Information provided by Iran Petrochemical Commercial Co.
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ISO 1184
Iran Petrochemical (PCC) Tabriz 1209AA LLDPE  (discontinued **)
Information provided by Iran Petrochemical Commercial Co.
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D882
Westlake Hifor SC74561-F Clear (Voridian) Polyethylene Film, Using Energx Technology Services  (discontinued *
VORIDIAN HIFOR CLEAR SC74558-F polymer is a high strength and high clarity polyethylene designed for blown film extrusion that contains medium slip and low antiblock additives. Films produced with t..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D882
Chevron Phillips HiD® 9638 HDPE Sheeting and Blown Film Resin  (discontinued **)
Resin Type: Sheeting Resin for the Geomembrane Market; ASTM D 4976 Classification: PE 225, A 56507Applications:Cast Geomembrane Applications, Notion and Millinery Bags, Heavy Duty Shipping Sacks, In..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D882
ExxonMobil Escorene® LD-333 EVA Film Resin, Very High Clarity, Very High Impact  (discontinued **)
Data provided by the manufacturer, Exxon Chemical.A 9.0% vinyl acetate copolymer film resin. Film made from LD-333 exhibits superior impact strength, clarity and heat sealability.Applications: Prim..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D882
NOVA Chemicals Novapol® TF-Y822-CP Hexene LLDPE Film Resin
Film Properties. Features: Good stiffness and machinability, exceptional toughness, suitable for narrow die gaps.Applications: Heavy duty sacks, high strength packaging.Data provided by the manufac..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D882
Petroquimica Triunfo Trilene® TS 8058 LLDPE-C6 and LDPE Blend
The Trilene TS 8058 product is a blend with a high ratio of linear low-density polyethylene - hexene comonomer (LLDPE-C6) with low-density polyethylene (LDPE) excellent mechanical resistance, along ..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ISO 527
Iran Petrochemical (PCC) LL0220AA Linear Low Density Polyethylene
LL 0220 AA is a LLDPE copolymer with butene as comonomer which contains anti-oxidant. This grade is suitable for the production of blown film for light duty applications and for the production of ca..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ISO 1184
SIDPEC EGYPTENE® LL 0220 AA LLDPE Film
Applications:Light and medium duty filmStretch filmFilm properties were measured on 38 micron film extruded at a blow up ratio of 2:1.Information provided by Interchim s.r.l., official distributor o..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ISO 1184
SIDPEC EGYPTENE® LL 0220 KJ LLDPE Film
Applications: Light and medium duty film.Film properties were measured on 38 micron film extruded at a blow up ratio of 2:1.Information provided by Interchim s.r.l., official distributor of Sidi Ke..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D882
SCG Chemicals EL-Leneâ„¢ H5615F High Density Polyethylene Film
Key Characteristics:High speed processingHigh tensile strengthHigh dart impactLow gel contentGood moisture barrierRecommended Applications: Ultra thin film (
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ISO 527-3
Borealis FG5199 Linear Low Density Polyethylene
FG5199 is a Butene Linear Low Density Polyethylene for Film Extrusion. Includes antioxidant, anti-Fog and cling additives. The grade is developed for blown cling film. Film made from FG5199 is suit..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ISO 527-3
Borealis FG5223 Linear Low Density Polyethylene
FG5223 is a Butene Linear Low Density Polyethylene for Film Extrusion. Includes antioxidant and anti-block additives. This grade is developed for production of lamination film. FG5223 has good heat..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
50 µm (2 mil) film; ASTM D882
DuPont Elvax® 3170 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film
18 wt% Vinyl Acetate.Elvax® 3170 is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resins..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
50 µm (2 mil) film; ASTM D882
DuPont Elvax® 3170SHB Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film
18 wt% Vinyl Acetate.Elvax® 3170SHB is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene res..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ISO 527-3
Total EVA 1010 VN 3 Ethylene Vinyl Acetate Copolymer - Blown Film
EVA 1010 VN 3 is made by a high pressure tubular process. Grade for films with high transparency and high mechanical properties. Contains an antioxidant.Application examples: Stretch film, food pa..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ISO 527-3
Total EVA 1020 VN 5 Ethylene Vinyl Acetate Copolymer - Blown Film
EVA 1020 VN 5 is made by a high pressure tubular process. Grade for very flexible films with very high transparency and good mechanical properties. Contains an antioxidant.Application examples: Ch..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
2 in per min; ASTM D882
Chevron Phillips MarFlex® D139 m-LLDPE Linear Low Density Polyethylene
Low Density PolyethyleneCustomer Benefits: Possesses the typical physical properties of metallocene polyethylenes with the added potential benefit of improved processability (bubble stability, down-..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
Calculated from mfr's report of 49 N/cm per ASTM D828 and the typical thickness
DuPont™ Nomex® E56 Paper, 7 mil Nominal Thickness
Nomex® Type E56 is designed for cost critical uses which require lesser amounts of mechanical and electrical strength than other Nomex® grades. It is thermally similar to Nomex® Type 410 but as..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D882
DuPont™ Surlyn® 1652 Zinc Ionomer Resin for Flexible Packaging
Surlyn® 1652 is an ionomer resin available for use in blown/cast film and extrusion coating operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylene ..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
Dow HDPE 05862N High Density Polyethylene
Film properties below based on a film thickness of 25 µm. Data provided by Dow Chemical.
Film Tensile Strength at Break, TD 28.0 - 50.0 MPa
4060 - 7250 psi
Average value: 42.2 MPa Grade Count:5
Overview of materials for High Density Polyethylene (HDPE), Injection Molded
This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Injection Molded". Each property range of values reported is minimum a..
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
50 µm (2 mil) film; ASTM D882
DuPont Elvax® 3173SHB Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film  (discontinued **)<
18 wt% Vinyl Acetate.Elvax® 3173SHB is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene res..