Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte™ 40LH247 OPP Film Product Description: A super white opaque, caviated BOPP film for Pressure Sensitive (PSA) labeling applications where superior optics are desired. LH247 also shows good performances on reel-fed wra.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte™ 50LH247 OPP Film Product Description: A super white opaque, cavitated BOPP film for Pressure Sensitive (PSA) labeling applications where superior optics are desired. 50LH247 also shows excellent performances on reel.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte™ 50LH538 Preliminary Data Sheet OPP Film Product Description: A super white opaque polypropylene film face stock with a proprietary caviated core providing high yield and excellent opacity. The coated print surface provides exceptional ink.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte™ 60ZH247 OPP Film Product Description: A super white opaque, caviated BOPP film for Pressure Sensitive (PSA) labeling applications where good optical properties are required. 60ZH247 also shows excellent performances.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte™ 65LT500 OPP Film Product Description: A matte finish, white polypropylene film designed or use in demanding thermal transfer, pressure-sensitive label and tag applications.Availability: Asia Pacific, Europe and Nort.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte™ 65LTR741 OPP Film Product Description: A biaxially oriented, white opaque multi-layer polypropylene film with an expanded core, and coated with a proprietary static resistant coating on one side. The non-coated gloss.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Label-Lyte™ 70LTR742 OPP Film Product Description: A matte finish, coated, white, polypropylene film designed for use in demanding thermal transfer, pressure-sensitive label applications. It is also compatible with a wide range .. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Oppalyte™ 40MH247 OPP Film Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film. This opaque and stiff film is ideal for mono material requirements and it has been especial.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Oppalyte™ 42AH748 OPP Film Product Description: A high barrier, high speed, super white opaque, modified higher density biaxially oriented polypropylene film, coated one side high barrier PVdC, one side very low temperature s.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Oppalyte™ 42MH647 OPP Film Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film, acrylic coated two sides. It provides outstanding performance on all packaging machines.Ava.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Oppalyte™ 42MH648 OPP Film Product Description: A high speed super white opaque, modified higher density, biaxially oriented polypropylene film, acrylic coated one side acrylic, one side very low temperature seal (VLTS) coati.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Oppalyte™ 50MH247 OPP Film Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film. This opaque and stiff film is ideal for mono material requirements and it has been especial.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Oppalyte™ 52MH647 OPP Film Product Description: A super white opaque, modified higher density, biaxially oriented polypropylene film, acrylic coated two sides. It provides outstanding performance on all packaging machines.Ava.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Oppalyte™ 52MH648 OPP Film Product Description: A high speed super white opaque, modified higher density, biaxially oriented polypropylene film, coated one side acrylic, one side very low temperature seal (VLTS) coating. VLTS.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Oppalyte™ 52MHR647 OPP Film Product Description: A super white opaque, modified higher density, biaxially oriented PP film, humidity resistant acrylic coated two sides. This film is designed to wrap products with a high moistu.. |
|||
Film Tensile Strength at Break, TD | 185 MPa | 26800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
ExxonMobil Oppalyte™ 60MH247 OPP Film Product Description: A super white opaque, modified higher density, biaxially oriented PP film. This opaque and stiff film is ideal for mono material requirements and it has been designed for cold s.. |