Polymer Property : Film Tensile Strength at Break, TD = 17400 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	120 MPa	17400 psi	ISO 527
Victrex® APTIV® 1000-050 Polyetheretherketone (PEEK) Polymer Film, Semi-Crystalline APTIV PEEK 1000 series films are the unfilled semi-crystalline films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTI..
Film Tensile Strength at Break, TD	120 MPa @Thickness 0.125 mm	17400 psi @Thickness 0.00492 in	ISO 527
Victrex® APTIV® 1000-050 Polyetheretherketone (PEEK) Polymer Film, Semi-Crystalline APTIV PEEK 1000 series films are the unfilled semi-crystalline films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTI..
Film Tensile Strength at Break, TD	120 MPa @Thickness 0.0250 mm	17400 psi @Thickness 0.000984 in	ISO 527
Victrex® APTIV® 1000-050 Polyetheretherketone (PEEK) Polymer Film, Semi-Crystalline APTIV PEEK 1000 series films are the unfilled semi-crystalline films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTI..
Film Tensile Strength at Break, TD	120 MPa	17400 psi	ISO 527
Victrex® APTIV® 2000-050 Polyetheretherketone (PEEK) Polymer Film, Amorphous APTIV PEEK 2000 series films are the unfilled amorphous films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTIV PEEK ..
Film Tensile Strength at Break, TD	120 MPa @Thickness 0.100 mm	17400 psi @Thickness 0.00394 in	ISO 527
Victrex® APTIV® 2000-050 Polyetheretherketone (PEEK) Polymer Film, Amorphous APTIV PEEK 2000 series films are the unfilled amorphous films made from VICTREX® PEEK polymer. The film provides a material solution for engineers in ultra-high performance applications.APTIV PEEK ..
Film Tensile Strength at Break, TD	120 MPa	17400 psi	20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 28LLG MET OPP Film Product Description: A clear, one-side metallized, one-side treated oriented polypropylene film. The metalized layer is designed to provide a bright metal appearance in surface print or laminated ap..
Film Tensile Strength at Break, TD	120 MPa	17400 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Label-Lyte™ 38DL247 OPP Film Product Description: A super white opaque, high gloss, high yield and highly cavitated BOPP film designed for use in reel-fed wrap-around labeling applications where superior graphics are desired.Av..
Film Tensile Strength at Break, TD	120 MPa	17400 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
ExxonMobil Oppalyte™ 38DO447 OPP Film Product Description: A super white opaque BOPP film. The Diamex technology allows for super low density and very high yield. Diamex makes it possible to lower the density, without decreasing the mod..
Film Tensile Strength at Break, TD	120 MPa	17400 psi	ASTM D882
Dow Saran® 540 Clear Plastic Barrier Film Saran™ 540 is a clear biaxially oriented monolayer barrier film, designed for unit packaging and other applications. It is available in 4 gauge.Information provided by Dow