Polymer Property : Film Tensile Strength at Yield, TD = 2320 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, TD	16.0 MPa	2320 psi	ISO 527-3
Polimeri Europa Flexirene® CM 50 Butene Copolymer Linear Low Density Polyethylene Flexirene CM 50 is a butene copolymer with medium density (C4-LLDPE), with antioxidants, suitable for cast film extrusion.Main Applications: Flexirene CM 50 is a highly stiff product and it is reco..
Film Tensile Strength at Yield, TD	16.0 MPa	2320 psi	ASTM D882
NOVA Chemicals Novapol® TD-9055-E Hexene LMDPE Film Resin Excellent stiffness and glossApplications: Diaper back sheet, BlendingAdditives: High temperature AOFilm properties are typical of cast film extruded at 280°C.Information provided by NOVA Chemicals..
Film Tensile Strength at Yield, TD	16.0 MPa	2320 psi	ASTM D882
NOVA Chemicals Novapol® TF-0338-E Hexene LMDPE Film Resin Excellent stiffness and glossApplications: Diaper back sheet, BlendingAdditives: High temperature AOFilm properties are typical of film extruded at 280°C.Information provided by NOVA Chemicals.
Film Tensile Strength at Yield, TD	16.0 MPa	2320 psi	ASTM D882
NOVA Chemicals Sclair® 14A Butene MDPE Film Resin (discontinued **) Film Properties. Features: Low gel, strength and toughness, broad MW distribution.Applications: Co-extrusion, blending.Data provided by the manufacturer.
Film Tensile Strength at Yield, TD	16.0 MPa	2320 psi	ASTM D882
ExxonMobil Escorene® LD-129 MDPE Cast Overwrap Film Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer film resin with good clarity and excellent stiffness. Film made from LD-129 can be used in overwrap applications and in push-through ..
Film Tensile Strength at Yield, TD	16.0 - 70.0 MPa	2320 - 10200 psi	Average value: 30.5 MPa Grade Count:6
Overview of materials for Styrene-Butadiene Copolymer, SBC This property data is a summary of similar materials in the MatWeb database for the category "Styrene-Butadiene Copolymer, SBC". Each property range of values reported is minimum and maximum values ..
Film Tensile Strength at Yield, TD	16.0 MPa	2320 psi	2 in per min; ASTM D882
Chevron Phillips K-Resin® KR10 Styrene-Butadiene Copolymer, Film Grade (discontinued **) Styrene-Butadiene Copolymer. Properties below based on 1 mil ( 0.025 mm) film; 2.5:1 Blow Up Ratio; 35 mil (0.90 mm) die gap.Customer Benefits: This SBC is easily processed on blown film or cast fi..
Film Tensile Strength at Yield, TD	16.0 MPa	2320 psi	2 in per min; ASTM D882
Chevron Phillips K-Resin® DK11 Styrene-Butadiene Copolymer, Film Grade Styrene-Butadiene Copolymer. Properties below based on 1 mil ( 0.025 mm) film; 2.5:1 Blow Up Ratio; 35 mil (0.90 mm) die gap.Customer Benefits: Provides the same high performance film properties as..
Film Tensile Strength at Yield, TD	16.0 - 36.0 MPa	2320 - 5220 psi	Average value: 25.3 MPa Grade Count:10
Overview of materials for Polypropylene, Sheet/Thermoforming Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Sheet/Thermoforming Grade". Each property range of values reported is minimum and maximum..
Film Tensile Strength at Yield, TD	16.0 MPa	2320 psi	2 in per min; ASTM D882
Chevron Phillips K-Resin® DK13 Styrene-Butadiene Copolymer, Film Grade (discontinued **) Styrene-Butadiene Copolymer. Properties below based on 1 mil ( 0.025 mm) film; 2.5:1 Blow Up Ratio; 35 mil (0.90 mm) die gap.Customer Benefits: DK13 is an SBC designed for the film market and has i..