Polymer Property : Film Tensile Strength at Yield, TD = 15.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi	ISO 527-3
Polimeri Europa Riblene® FM 50 Low Density Polyethylene - Blown Film Extrusion Riblene FM 50 is a low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FM 50 is characterized by optimum optical properties and rigidity.Films manufactured with Riblene FM 50..
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi	ISO 527-3
Polimeri Europa Riblene® FM 53 Low Density Polyethylene - Blown Film Extrusion Riblene FM 53 is a low density polyethylene (LDPE) with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FM 53 is characterized by optimum optical properties and rigid..
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi	ISO 527
Premix Thermoplastics PRE-ELEC® PE 1271 PRE-ELEC PE 1271 is a conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivi..
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi	ASTM D 882
NOVA Chemicals Novapol® TF-0438-E Hexene LMDPE Film Resin TF-0438-E complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food, without temperatur..
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi	ISO 527
Premix Thermoplastics PRE-ELEC® PE 1308 (discontinued **) PRE-ELEC PE 1308 is a conductive thermoplastic compound based on a blend of PE-LD/PE-LLD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivi..
Film Tensile Strength at Yield, TD	15.0 MPa	2170 psi	at 2% offset; ASTM D882
ExxonMobil LD 117.03 Blown Overwrap Film Resin (discontinued **) LD 117 resins are homopolymer film resins with good clarity and excellent stiffness. Film from LD 117 resins can be used in overwrap applications and push-through type packaging equipment. Film ma..
Film Tensile Strength at Yield, TD	15.0 MPa	2170 psi	at 2% offset; ASTM D882
ExxonMobil LD 117.08 Blown Overwrap Film Resin (discontinued **) LD 117 resins are homopolymer film resins with good clarity and excellent stiffness. Film from LD 117 resins can be used in overwrap applications and push-through type packaging equipment. Film ma..
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi	ASTM D882
NOVA Chemicals Sclair® 14K1 Octene LMDPE Film Resin (discontinued **) Film Properties. Features: Low gel, excellent optics, good moisture barrier.Applications: Cast overwrap film.Data provided by the manufacturer.
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi	ASTM D882
NOVA Chemicals Sclair® 14K3 Octene LMDPE Film Resin (discontinued **) Film Properties. Features: Low gel, excellent optics, good moisture barrier.Applications: Cast overwrap film.Data provided by the manufacturer.
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi	ASTM D882
ExxonMobil Escorene® LD-117 MDPE Blown Overwrap Film Resin, Tough (discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer film resin with good clarity and excellent stiffness. Film made from LD-117 can be used in overwrap applications and in push-through ..
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi	ASTM D882
Iran Petrochemical (PCC) 235F7 Linear Low Density Polyethylene 235F7 is a LLDPE blown film grade designed for general purpose film application. This resin is particularly suited for blending with LDPE, giving better strength and downgauging possibility.Informat..
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi	ISO 527-3
Total Lumicene® mPE M 2704 EP S01 Metallocene Polyethylene, Blown Film This product is a Total Ecosolutions grade.Lumicene® mPE M 2704 EP S01 is a second generation metallocene based Low Density Polyethylene with hexene as comonomer.Lumicene® mPE M 2704 EP S01 can be..
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi
Dow DOWLEX™ 2071 Linear Low Density Polyethylene DOWLEX® 2071 Polyethylene resin is a linear low density polyethylene resin specifically designed for the manufacture of high strength, thin gauge films for use in applications such as grocery sacks..
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi
Dow Elite® 5110 Linear Low Density Polyethylene 5110 enhanced polyethylene resin is a copolymer produced via INSITE Technology from Dow Plastics. It offers unique combination of high modulus and excellent impact strength, allowing for downgaugin..
Film Tensile Strength at Yield, TD	15.0 MPa	2170 psi	at 2% offset; ASTM D882
ExxonMobil LL 3201.22 Premium High Strength Film Resin (discontinued **) LL 3201 resins are hexene copolymer LLDPE film resins. Films produced from these resins have excellent tensile, toughness and stiffness properties. These strength properties, along with good drawdow..
Film Tensile Strength at Yield, TD	15.0 - 18.0 MPa	2180 - 2610 psi	Average value: 16.9 MPa Grade Count:16
Overview of materials for Linear Medium Density Polyethylene (LMDPE), Film This property data is a summary of similar materials in the MatWeb database for the category "Linear Medium Density Polyethylene (LMDPE), Film". Each property range of values reported is minimum and..
Film Tensile Strength at Yield, TD	15.0 MPa	2180 psi	ASTM D882
NOVA Chemicals Novapol® TF-Y529-BP Hexene LLDPE (discontinued **) Puncture value is 50 J/mm. Hexene LLDPE. Excellent puncture resistance, good stiffness and machinability, and good tensile properties. Additive Package: High slip and antiblock, process aid.Applic..