Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 9.72 GPa | 1410 ksi | ASTM D638 |
Solvay Specialty Polymers Kadel® E-1130 Polyketone
(discontinued **) High performance proprietary semi-crystalline polymer based resins with exceptional solvent resistance and high temperature performance. They provide strength and stiffness, plus superior chemical r.. |
|||
Tensile Modulus | 9.72 GPa | 1410 ksi | ASTM D638 |
LNP Thermocomp® LF-1006 MG Polyetheretherketone, Glass milled Glass Fiber
(discontinued **) Features: Low WarpageForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still a.. |
|||
Tensile Modulus | 9.72 GPa | 1410 ksi | ASTM D1708 |
Solvay Specialty Polymers Torlon® 4435 Polyamide-imide (PAI)
(Unverified Data**) Torlon 4435 is a polyamide-imide resin specifically designed to provide exceptionally low wear performance in non-lubricated applications even at high pressure and velocity (PV) conditions. Not only.. |
|||
Tensile Modulus | 9.72 GPa | 1410 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP IFP36 PA6.12 LNP* LUBRICOMP* IFP36 is a Nylon 6/12 base resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of t his grade include: Wear Resistant. |
|||
Tensile Modulus | 9.72 GPa | 1410 ksi | ISO 527 |
Solvay Technyl® C 218 MT25 V15 25% Mineral, 15% Glass Filled, Heat Stabilized Nylon 6 Information provided by Rhodia; Rhodia has been acquired by Solvay. |
|||
Tensile Modulus | 9.72 GPa | 1410 ksi | ASTM D638 |
Solvay Technyl® C216V30 30% Glass Filled Nylon 6 Information provided by Rhodia; Rhodia has been acquired by Solvay. |
|||
Tensile Modulus | 9.72 GPa | 1410 ksi | ASTM D638 |
Solvay Specialty Polymers Torlon® 4435 Polyamide-imide (PAI) Torlon® 4435 is a polyamide-imide resin specifically designed to provide exceptionally low wear performance in non-lubricated applications even at high pressure and velocity (PV) conditions. Not .. |