Polymer Property : Tensile Modulus = 9.58 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 9.58 GPa
1390 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL36 PC
LNP* LUBRICOMP* DFL36 is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Tensile Modulus 9.58 GPa
1390 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL36HL PC (Asia Pacific)
LNP* LUBRICOMP* DFL36HL is a compound based on Polycarbonate resin containing PTFE, Glass Fiber. Added features of this material include: Internally Lubricated.
Tensile Modulus 9.58 GPa
1390 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL36XXP PC
LNP* Lubricomp* DFL36XXP is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Tensile Modulus 9.58 GPa
1390 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10
LNP LUBRICOMP* QCL329 is a compound based on Nylon 6/10 resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.This data was supplied..
Tensile Modulus 9.58 GPa
1390 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10 (Asia Pacific)
LNP LUBRICOMP* QCL329 is a compound based on Nylon 6/10 resin containing Carbon Fiber, PTFE, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied..
Tensile Modulus 9.58 GPa
1390 ksi
ISO 527
Solvay Technyl® C218V30 30% Glass Filled, Heat Stabilized Nylon 6
Information provided by Rhodia; Rhodia has been acquired by Solvay.
Tensile Modulus 9.58 GPa
1390 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP IF006 PA 6/12
LNP THERMOCOMP* IF006 is a compound based on Nylon 6/12 resin containing 30% Glass Fiber.
Tensile Modulus 9.58 GPa
1390 ksi
50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp IF006S PA 6/12 (Asia Pacific)
LNP* Thermocomp* IF006S is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Paci..
Tensile Modulus 9.58 GPa
1390 ksi
50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp OF004AER PPS
LNP* Thermocomp* OF004AER is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SA..
Tensile Modulus 9.58 GPa
1390 ksi
ASTM D638
LNP Thermocomp® IF-1006 Polyamide 6/12 Copolymer, Glass Fiber Reinforcement  (discontinued **)
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names..
Tensile Modulus 9.58 GPa
1390 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON QEL329 PA 6/10
LNP STAT-KON* QEL329 is a compound based on Nylon 6/10 resin containing 10% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant, Flame Retardant..
Tensile Modulus 9.58 GPa
1390 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON QEL329 PA 6/10 (Asia Pacific)
LNP STAT-KON* QEL329 is a compound based on Nylon 6/10 resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.
Tensile Modulus 9.58 GPa
1390 ksi
50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp IF006S PA6.12
LNP* Thermocomp* IF006S is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas ..