Polymer Property : Tensile Modulus = 8.75 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	8.75 GPa	1270 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP WFL34H PBT LNP LUBRICOMP* WFL34H is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Healthcare.
Tensile Modulus	8.75 GPa	1270 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DEP42E PC LNP STAT-KON* DEP42E is a compound based on Polycarbonate resin containing 10% Carbon Fiber, 20% PTFE/Silicone. Added features of this material include: Easy Molding. Electrically Conductive, Wear..
Tensile Modulus	8.75 GPa	1270 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DEP42E PC (Asia Pacific) LNP STAT-KON* DEP42E is a compound based on Polycarbonate resin containing Silicone, PTFE, Carbon Fiber. Added features of this material include: Easy Molding.
Tensile Modulus	8.75 GPa	1270 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP IF006L PA 6/12 (Asia Pacific) LNP* THERMOCOMP* IF006L is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Low Extractible.
Tensile Modulus	8.75 GPa	1270 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP IF006L PA6.12 LNP* THERMOCOMP* IF006L is a compound based on Nylon 6/12 resin containing 30% Glass Fiber. Added features of this material include: Low Extractible.
Tensile Modulus	8.75 GPa	1270 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF006 PA 6 LNP THERMOCOMP* PF006 is a compound based on Nylon 6 resin containing 30% Glass Fiber.
Tensile Modulus	8.75 GPa	1270 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF006S PA 6 LNP THERMOCOMP* PF006S is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Modulus	8.75 GPa	1270 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP PF006U PA 6 LNP THERMOCOMP* PF006U is a compound based on Nylon 6 resin containing 30% Glass Fiber. Added features of thie grade are: UV Stabilized.
Tensile Modulus	8.75 GPa	1270 ksi	1 mm/min
Arkema Group Rilsan® AZM 30 GT8LD Nylon 12, 30% Glass Fiber Filled (Dry) Designation ISO 1874-PA12,MHLS,16-050,(G+C)(F+D)(30+05)Rigid grade with glass fiber (30%) and graphite filler for injection molding. Available color: steel black gray. Reinforced light and heat stab..