Polymer Property : Tensile Modulus = 679 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 4.68 GPa
679 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2100 PEI
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification in recognized colors.
Tensile Modulus 4.68 GPa
679 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2100 PEI (Asia Pacific)
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification in recognized colors.
Tensile Modulus 4.68 GPa
679 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2100F PEI
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. US FDA and EU Food Contact Compliant, NSF 51 listing. WRAS certification in recognized col..
Tensile Modulus 4.68 GPa
679 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2100F PEI (Asia Pacific)
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. US FDA and EU Food Contact Compliant, NSF 51 listing, WRAS certification in recognized colors..
Tensile Modulus 4.68 GPa
679 ksi
5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 2100N PEI
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
Tensile Modulus 4.68 GPa
679 ksi
5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 2100N PEI (Asia Pacific)
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Modulus 4.68 GPa
679 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2100R PEI
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Tensile Modulus 4.68 GPa
679 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2100R PEI (Asia Pacific)
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Tensile Modulus 4.68 GPa
679 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU2100 PEI
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). US FDA and European Food Contact approved. For medical devices and pharmaceutical applications.Healthcare management of change, biocom..
Tensile Modulus 4.68 GPa
679 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU2100 PEI (Asia Pacific)
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). US FDA and European Food Contact approved. For medical devices and pharmaceutical applications.Healthcare management of change, biocom..
Tensile Modulus 4.68 GPa
679 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU2100 PEI (Europe-Africa-Middle East)
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). US FDA and European Food Contact approved. For medical devices and pharmaceutical applications.Healthcare management of change, biocom..
Tensile Modulus 4.68 GPa
679 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP QFL32 PA 6/10
LNP* LUBRICOMP* QFL32 is a compound based on Nylon 6/10 containing 10% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant.
Tensile Modulus 4.68 GPa
679 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP JF002 PES
LNP THERMOCOMP* JF002 is a compound based on Polyethersulfone resin containing 10% Glass Fiber.