Polymer Property : Tensile Modulus = 669 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 4.61 GPa
669 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2110 PEI (Asia Pacific)
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.
Tensile Modulus 4.61 GPa
669 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU2110 PEI
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP ..
Tensile Modulus 4.61 GPa
669 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP DF0029P PC
LNP THERMOCOMP* DF0029P is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Exceptional Processing. Flame Retardant.
Tensile Modulus 4.61 GPa
669 ksi
5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 2110N PEI (Asia Pacific)
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Modulus 4.61 GPa
669 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2110R PEI
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Tensile Modulus 4.61 GPa
669 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2110R PEI (Asia Pacific)
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Tensile Modulus 4.61 GPa
669 ksi
1mm/min; ISO 527
BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Conditioned)
Ultramid 8333G HI is a 14% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance of st..
Tensile Modulus 4.61 GPa
669 ksi
1mm/min; ISO 527
BASF Ultramid® 8333G HI HS BK-102 33% Glass Filled PA6 (Conditioned)
Ultramid 8333G HI HS BK-102 is a 33% glass reinforced, heat stabilized, impact modified, pigmented black, PA6 injection molding compound developed for applications requiring improved dry as molded t..
Tensile Modulus 4.61 GPa
669 ksi
Applied Nanostructured Solutions Carbon NanoStructure Encapsulated Flakes
Carbon NanoStructure (CNS) Encapsulated Flakes are a unique form of carbon nanotubes, produced using a proprietary ANS process. The ANS process creates cross-linked multiwall carbon nanotube-based n..
Tensile Modulus 4.61 GPa
669 ksi
same value from ASTM and ISO test.
BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)  (discontinued **)
Capron 8333G HI is a 33% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance ..
Tensile Modulus 4.61 GPa
669 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2110 PEI
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.
Tensile Modulus 4.61 GPa
669 ksi
5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 2110N PEI
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Americas region.