Polymer Property : Tensile Modulus = 5.80 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	0.0400 GPa	5.80 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Lubricomp TX03476 PU LNP* Lubricomp* TX03476 is a Polyurethane containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region.
Tensile Modulus	0.0400 GPa	5.80 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP Lubricomp TX03476 PU LNP* Lubricomp* TX03476 is a Polyurethane containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region.
Tensile Modulus	0.0400 GPa	5.80 ksi	in plane; ASTM D638
SABIC Innovative Plastics ULTEM Foam XP110 PEI ULTEM foam is a polyetherimide based thermoplastic foam with excellent flame, smoke and toxicity performance. The material combines a high strength to weight ratio with low moisture absorption. The ..
Tensile Modulus	0.0400 GPa	5.80 ksi	1 mm/min; ASTM D638 - ISO 527-2
DuPont Elvaloy® 2116 AC Ethylene and 16% Ethyl Acrylate Copolymer Elvaloy® 2116 AC is intended for profile and tube extrusion. Its good chemical resistance, low temperature toughness and good flex life make it outstanding for specialty tubing. The material also..
Tensile Modulus	0.0400 GPa	5.80 ksi	1 mm/min; ASTM D638 - ISO 527-2
DuPont Elvaloy® 3117 AC Ethylene and 17% Butyl Acrylate Copolymer Elvaloy® 3117 AC is intended for coextrusion and compounding. Due to its high melt flow rate, it is used also in extrusion coating. Elvaloy® 3117 AC is soft, flexible and has good adhesion to va..
Tensile Modulus	0.0400 GPa	5.80 ksi	1 mm/min; ASTM D638 - ISO 527-2
DuPont Elvaloy® 3717 AC Ethylene and 17% Butyl Acrylate Copolymer Elvaloy® 3717 AC can be used for coextrusion, compounding and injection molding. In coextrusion, it can be used to improve sealing; in compounding, to improve low temperature and impact properties..
Tensile Modulus	0.0400 GPa	5.80 ksi	1 mm/min; ASTM D638 - ISO 527-2
DuPont Elvaloy® 2615 AC Ethylene and 15% Ethyl Acrylate Copolymer Because of its high flexibility and high filler loading capacity, Elvaloy® 2615 AC is particularly suited for injection molded parts in the automotive and furniture industries. It also offers exce..
Tensile Modulus	0.0400 GPa	5.80 ksi
BASF Styrodur® 5000 CS Extruded Rigid Polystyrene Foam (Europe) Description: Styrodur C is the green extruded rigid polystyrene foam (XPS) from BASF. As a thermal insulation, it makes a significant contribution to climate protection by reducing CO2 emissions. Th..
Tensile Modulus	>= 0.0400 GPa	>= 5.80 ksi	in the plane; ISO 527 1-2
3A Composites Core Materials AIREX® C71.75 Elevated Temperature Structural Foam AIREX® C71 is a closed cell, crosslinked polymer foam especially formulated to maintain its stability also at higher processing or service temperatures. It combines excellent stiffness and strength..