Polymer Property : Tensile Modulus = 4.34 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	4.34 GPa	630 ksi	ASTM D638
Quadrant EPP Ketron® 1000 LSG PEEK, Biocompatibility tested (ISO Product Data Sheet) KETRON® PEEK LSG natural / black stock shapes are produced from batches of Victrex PEEK. This material exhibits a unique combination of mechanical properties, temperature and chemical resistance. ..
Tensile Modulus	4.34 GPa	630 ksi	ASTM D638
Quadrant EPP Ketron® 1000 LSG PEEK, Extruded Unfilled Polyetherether Ketone (ASTM Product Datasheet)
Tensile Modulus	4.34 GPa	630 ksi	ASTM D638
Quadrant EPP Ketron® 1000 PEEK, Extruded Unfilled Polyetherether Ketone (ASTM Product Data Sheet)
Tensile Modulus	4.34 GPa	629 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP Faradex ES003DE PEI LNP* Faradex* ES003DE is a Polyetherimide resin containing stainless steel fibers. Characteristics of this grade are EMI/RFI Shielding.This data was supplied by SABIC-IP for the Americas region.
Tensile Modulus	4.34 GPa	629 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP FARADEX ES003E PEI LNP* FARADEX* ES003E is a Polyetherimide resin containing 15% Stainless Steel Fibers. Added feature of this grade is: EMI/RFI Shielding.
Tensile Modulus	4.34 GPa	629 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Lubricomp DFL329EF PC LNP LUBRICOMP* DFL329EF is a compound based on Polycarbonate resin containing Flame Retardant, Glass Fiber, PTFE. Added features of this material include: Flame Retardant.This data was supplied by ..
Tensile Modulus	4.34 GPa	630 ksi	ASTM D638
Quadrant EPP Ketron® LSG PEEK-CLASSIX Biocompatibility tested (ASTM Product Data Sheet) KETRON® PEEK-CLASSIX LSG white stock shapes are produced from Invibio® PEEK-CLASSIX White resin. This material exhibits a unique combination of mechanical properties, temperature and chemical re..
Tensile Modulus	4.34 GPa	629 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM AR9100 PEI (Asia Pacific) 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
Tensile Modulus	4.34 GPa	629 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP AX90213 ABS LNP* THERMOCOMP* AX90213 is a compound based on ABS resin containing Glass Fiber.
Tensile Modulus	4.34 GPa	629 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP AX90213 ABS (Asia Pacific) LNP* Thermocomp* AX90213 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber.
Tensile Modulus	4.34 GPa	629 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GTX GTX675 PPE+PA6 Noryl GTX* GTX675 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to a..
Tensile Modulus	4.34 GPa @Temperature 23.0 °C	629 ksi @Temperature 73.4 °F	EN ISO 527
Ensinger TECASINT 1041 Polyimide, 30% MoS2 Filled (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Tensile Modulus	4.34 GPa	629 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL329 PC LNP LUBRICOMP* DFL329 is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated.
Tensile Modulus	4.34 GPa	629 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM AR9100 PEI 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.