Polymer Property : Tensile Modulus = 255 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 1.76 GPa
255 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP ML004S PP (Asia Pacific)
LNP* Lubricomp* ML004S is a compound based on Polypropylene resin containing PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized.
Tensile Modulus 1.76 GPa
255 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON MX01767C PP
LNP* STAT-KON* MX01767C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System.
Tensile Modulus 1.76 GPa
255 ksi
5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON MX10301C PP
LNP* STAT-KON* MX10301C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System.
Tensile Modulus 1.76 GPa
255 ksi
5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp MX01767C PP
LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB..
Tensile Modulus 1.76 GPa
255 ksi
1 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp MX01767C PP
LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB..
Tensile Modulus 1.76 GPa
255 ksi
ASTM D 638
Styrolution PS 5310 HIPS
Excellent ESCRGood ToughnessMatte easily decorated finishInformation provided by Styrolution
Tensile Modulus 1.76 GPa
255 ksi
ASTM D638
Teknor Apex Terraloy™ BP 18003A Thermoplastic Starch + HIPS
Notes: Terraloy™ BP-18003A is a Thermoplastic Starch/HIPS ready-to-process compound that contains up to 30% of TPS renewable content. This compound is intended for injection molding application. P..
Tensile Modulus 1.76 GPa
255 ksi
5 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Stat-kon MX01767C PP
LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB..