Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 8.80 GPa | 1280 ksi | |
Plastcom SLOVAMID 6 GF 30 HI PA6, 30% glass fibre, improved strength FeaturesPA 6 for injection moulding, chemically strengthened with 30% glass fibre and with the content of thermoplastic kaoutchouc. Application: impacted mouldings and mouldings with high strength a.. |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | 50 mm/min; ASTM D638 |
Ovation Polymers Opnyl OP6GF50 Nylon 6, 50% Glass Reinforced, Dry Nylon 6 - Glass reinforced (50 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m.. |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | ISO 527 |
Nilit FRIANYL A63 HH-FK 2020 Nylon 6.6 for injection molding, 20% glass fiber and 20% glass ball reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | ISO 527 |
Nilit FRIANYL B63 H-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Modulus | 8.80 GPa @Temperature 23.0 °C |
1280 ksi @Temperature 73.4 °F |
ISO 527 |
Victrex® PEEK 450GL20 Polyetheretherketone, 20% Glass Fibre Reinforced Product Description:High performance thermoplastic material, 20% carbon fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, .. |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | ISO 527-2 |
Pasargad Polymer Peyvand Pasamid 3P-H1130B Nylon 6, 30% Glass Fiber Reinforced Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | ISO 527-2 |
Pasargad Polymer Peyvand Pasamid 3P-H7130B Nylon 6/66, 30% Glass Fiber Reinforced Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Electrical PartsFastenerHousingInformation provided by Pasargad Polymer Peyvand Co |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | 1 mm/min; ISO 527-1,-2 |
Gromax BFG30-FH00B2 Nylon 6 30% Glass Filled (Dry) Information provided by Gromax Enterprises Corp. |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | ISO 527-1/-2 |
Lanxess Durethan® AKV 325 H2.0 901510 Nylon 66, 25% Glass Fiber PA 66, 25% glass fibers, extrusion- and blow molding grade, branched, high viscosity, good heat-ageing resistance, good hydrolysis resistance |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | |
LATI Latilub 62-01M G/30 PA6, 30% Glass Fiber Reinforced Self-lubricating product based on Polyamide 6 (PA6). Molybdenum disulphide. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided b.. |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | ISO 527 Type 1A |
Solvay TECHNYL® A 30 H1 V25 PA66, 25% glass fiber, DRY Description: Flame-retardant polyamide 66, 25% glass-fiber reinforced, heat stabilized for injection molding.Available in: Asia Pacific, Europe, Latin America and North America Product Applications:.. |
|||
Tensile Modulus | 8.82 GPa | 1280 ksi | 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10 LNP LUBRICOMP* QCL329 is a compound based on Nylon 6/10 resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.This data was supplied.. |
|||
Tensile Modulus | 8.82 GPa | 1280 ksi | 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp QCL329 PA 6/10 (Asia Pacific) LNP LUBRICOMP* QCL329 is a compound based on Nylon 6/10 resin containing Carbon Fiber, PTFE, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied.. |
|||
Tensile Modulus | 8.84 GPa | 1280 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® K4560 PBT (Europe-Africa-Middle East) 30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable. |
|||
Tensile Modulus | 8.84 GPa | 1280 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP DX13354 PC COPOLYMER (Asia Pacific) DX13354 is 30% glass fiber reinforced, impact modified and LDS functionalized polycarbonate resin. The features include LDS function, high flow, and good ductility. |
|||
Tensile Modulus | 8.83 GPa | 1280 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP IX04513C PA 6/12 (Asia Pacific) LNP THERMOCOMP* IX04513C is a compound based on Nylon 6/12 resin containing Glass Fiber. Added features of this material include: Clean Compounding System. |
|||
Tensile Modulus | 8.83 GPa | 1280 ksi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® AR-5300H PBT/ASA, 30% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP QF006 PA 6/10 LNP THERMOCOMP* QF006 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber. |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp RF006EU PA 66 (Europe-Africa-Middle East) LNP* THERMOCOMP* RF006EU is a compound based on PA 66 resin containing Glass Fiber. Added features include: Easy Molding, UV-StabilizedThis data was supplied by SABIC-IP for the Europe-Africa-Middle.. |
|||
Tensile Modulus | 8.83 GPa | 1280 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp WF006SXC PBT LNP* Thermocomp* WF006SXC is a compound based on PBT containing Glass FIber. Characteristic of this grade is: Heat Stabilized.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | ASTM D638 |
Plenco 2369 Phenolic, Granular, Compression Molded PLENCO 02369 is a general purpose, organic filled phenolic molding compound, formulated to minimize the generation of free ammonia for applications that are sensitive to such formation. PLENCO 02369.. |
|||
Tensile Modulus | 8.81 GPa | 1280 ksi | ISO 527 |
Polyram PlusTek PA7800G33 Nylon 6.6 for Injection Molding, 33% Glass Fiber Reinforced, Heat Stabilized, Impact Modified 33% Glass fiber reinforced, heat stabilized, impact modified Nylon 6.6 for injection molding applications.Information provided by Polyram. |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | 1 mm/min; ISO 527 |
Eurostar Starflam BFR460A PA6, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam BFR460A is a Flame Retardant, Glass Fiber Reinforced Polyamide 6, Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | 1 mm/min; ISO 527 |
Eurostar Staramide RF006EU PA66/6, Glass Fiber Filled, Injection Molded Staramide RF006EU is an UV stabilized, Glass Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as Staramide 66C 30V S4)Information provided by Eurostar. |
|||
Tensile Modulus | 8.80 GPa | 1280 ksi | 1 mm/min |
Arkema Group Orgalloy® RS 6630 Nylon 66 Alloy, 30% Glass Fiber (Conditioned) RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional propertie.. |
|||
Tensile Modulus | 8.82 GPa | 1280 ksi | 1 mm/min |
Arkema Group Rilsan® AZM 30 O TLD Nylon 12, 30% Glass Fiber Filled (Dry) Designation ISO 1874-PA12,MHLR,16-050,GF30Rigid grade with glass fiber (30%) for injection molding. Available color: natural. Light and heat stabilizing agent. Mold-release agent.High rigidity. High.. |
|||
Tensile Modulus | 8.83 GPa | 1280 ksi | ASTM D638 |
Techmer Lehvoss Compounds Luvotech™ J-4/35 NAT PA6/12
(discontinued **) Techmer Lehvoss Compounds, a JV between Techmer ES and Lehmann&Voss&Co. has been terminated. |
|||
Tensile Modulus | 8.82 GPa | 1280 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON QEL329 PA 6/10 LNP STAT-KON* QEL329 is a compound based on Nylon 6/10 resin containing 10% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant, Flame Retardant.. |
|||
Tensile Modulus | 8.83 GPa | 1280 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Verton MV00ASUV_WH9D703 PP Preliminary data for 50% Long fiber single color pellet filled PPThis data was supplied by SABIC-IP for the Americas region. |