Polymer Property : Tensile Modulus = 11.17 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	11.17 GPa	1620 ksi	same value from ASTM and ISO test.
BASF Capron® HPN 9233G 33% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron HPN 9233G is a 33% glass reinforced polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with excellent surface aesthetics. It is..
Tensile Modulus	11.17 GPa	1620 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF008ER PC LNP THERMOCOMP* DF008ER is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features include: Easy Molding, Mold Release.
Tensile Modulus	11.17 GPa	1620 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF007H PA 66 LNP* Thermocomp* RF007H is a compound based on Nylon 66 containing glass fiber. Added feature includes: Healthcare.
Tensile Modulus	11.17 GPa	1620 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF007SXP PA 66 LNP* THERMOCOMP* RF007SXP is a compound based on Nylon 66 containing 35% Glass Fiber. Added feature of this material includes: Heat Stabilized.
Tensile Modulus	11.17 GPa	1620 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF008ERH PC LNP THERMOCOMP* DF008ERH is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Healthcare.
Tensile Modulus	11.17 GPa	1620 ksi	50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP MC002 PP LNP* THERMOCOMP* MC002 is a compound based on Polypropylene resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive.