Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Modulus | 1.76 GPa | 255 ksi | 50 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP ML004S PP (Asia Pacific) LNP* Lubricomp* ML004S is a compound based on Polypropylene resin containing PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized. |
|||
Tensile Modulus | 1.76 GPa | 255 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON MX01767C PP LNP* STAT-KON* MX01767C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System. |
|||
Tensile Modulus | 1.76 GPa | 255 ksi | 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON MX10301C PP LNP* STAT-KON* MX10301C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System. |
|||
Tensile Modulus | 1.76 GPa | 255 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp MX01767C PP LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB.. |
|||
Tensile Modulus | 1.76 GPa | 255 ksi | 1 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp MX01767C PP LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB.. |
|||
Tensile Modulus | 1.76 GPa | 255 ksi | ASTM D 638 |
Styrolution PS 5310 HIPS Excellent ESCRGood ToughnessMatte easily decorated finishInformation provided by Styrolution |
|||
Tensile Modulus | 1.76 GPa | 255 ksi | ASTM D638 |
Teknor Apex Terraloy™ BP 18003A Thermoplastic Starch + HIPS Notes: Terraloy™ BP-18003A is a Thermoplastic Starch/HIPS ready-to-process compound that contains up to 30% of TPS renewable content. This compound is intended for injection molding application. P.. |
|||
Tensile Modulus | 1.76 GPa | 255 ksi | 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Stat-kon MX01767C PP LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB.. |