Polymer Property : Tensile Modulus = 0.230 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Modulus 0.230 GPa

@Temperature 23.0 °C
33.4 ksi

@Temperature 73.4 °F
ISO 527
DuPont Performance Polymers Hytrel® DYM250S BK472 TPC-ET  (Unverified Data**)
Hytrel® DYM250S BK472 is a medium modulus resin suited for injection molding of Air Bag Deployment Doors. It has a nominal durometer hardness of 49D and contains fine particle size carbon black.In..
Tensile Modulus 0.230 GPa
33.4 ksi
ISO 527
FKuR Kunststoff Bio-Flex® F 1110 Compostable PLA Blend
The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta..
Tensile Modulus 0.230 GPa
33.4 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP YL003 Polyester Elastomer
LNP* LUBRICOMP* YL003 is a compoudn based on Polyester Elastomer resin containing 15% PTFE. Added feature of this grade is: Wear Resistant.
Tensile Modulus 0.230 GPa
33.4 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP TH0300A PUR
LNP THERMOCOMP* TH0300A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
Tensile Modulus 0.230 GPa
33.4 ksi
50 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP TH0300A PUR (Asia Pacific)
LNP THERMOCOMP* TH0300A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
Tensile Modulus 0.230 GPa
33.4 ksi
MD; ASTM D882-A
Borealis FT5230 Low Density Polyethylene
FT5230 is a Low Density Polyethylene for Film Extrusion. This grade is developed for the production of packaging film with good optical properties for medium duty film applications. Applications: ..
Tensile Modulus 0.230 GPa
33.4 ksi
MD; ASTM D882-A
Borealis FT5231 Low Density Polyethylene
FT5231 is a Low Density Polyethylene for blown film. Tubular technology. Contains Antioxidant. This grade is developed for the production of packaging film with good optical properties for medium d..
Tensile Modulus 0.230 GPa
33.4 ksi
MD; ASTM D882-A
Borealis FT5232 Low Density Polyethylene
FT5232 is a Low Density Polyethylene for Film Extrusion. Tubular Technology. Includes medium slip additive and antioxidant. This grade is developed for the production of packaging film with good op..
Tensile Modulus 0.230 GPa
33.4 ksi
MD; ASTM D882-A
Borealis FT5236 Low Density Polyethylene
FT5236 is a Low Density Polyethylene for Film Extrusion. Tubular Technology. Includes anti-block, antioxidant and medium slip additives. Applications FT5236 has been developed especially for applic..
Tensile Modulus 0.230 GPa
33.4 ksi
Bending Modulus; ASTM D790
UBE UMERIT 613A Metallocene LLDPE
Description: UBE Super Polyethylene Umerit® is an ethylene-olefin copolymer made by UBE using the metallocene catalytic method. The metallocene catalytic method results in superior physical propert..
Tensile Modulus 0.230 GPa
33.4 ksi
Through Plane Direction
Cymat A35620SC 020SS Stabilized Aluminum Foam
Description: Cymat A35620SC 020SS stabilized aluminum foam (SAF) is a closed cell aluminum foam formed from A356 aluminum alloy with a density of 0.2 g/cm3. The mechanical properties of SAF make it ..
Tensile Modulus 0.230 GPa

@Temperature 80.0 °C
33.4 ksi

@Temperature 176 °F
ISO Data
BASF Ultramid® 8254 HS BK-102 PA6 (Conditioned)
Ultramid 8254 HS is a highly flexible, heat stabilized, impact modified nylon 6 extrusion grade for tubing applications.
Tensile Modulus 0.230 GPa
33.4 ksi
average; in the plane; ISO 527 1-2
3A Composites Core Materials AIREX® C70.250 Universal Structural Foam
AIREX® C70 is a closed cell, crosslinked polymer foam that combines excellent stiffness and strength to weight ratios with superior toughness. It is non-friable, contains no CFC’s, has negligible ..
Tensile Modulus 0.230 GPa
33.4 ksi
average; perpendicular to plane; ASTM C297
3A Composites Core Materials AIREX® T92.200 Easy Processing Structural Foam
AIREX® T92 is a closed-cell, thermoplastic and recyclable polymer foam with good mechanical properties and price / performance ratio. It has a good resistance to fatigue, is chemically stable, UV r..
Tensile Modulus 0.230 GPa
33.4 ksi
ISO 527-1/-2
DSM Arnitel® CM622 TPC-ES
60 Shore D, Extrusion
Tensile Modulus 0.230 GPa
33.4 ksi
ASTM D638
Elastomer Engineering Elastamide 400 Elastomer Modified RIM Nylon 6
18% crystallinity. Information supplied by Elastomer Engineering.