Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 50 mm/min; ASTM D638 |
Ovation Polymers Nima™ HL 30525 GF FR PET, 25% Glass Fiber PET – Flame Retardant 25% Short Glass Fiber Reinforced. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to ASTM s.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | ASTM D638 |
NOVA Chemicals Dylark® 238P20 High Performance Glass Filled Styrenic Very high modulus, High heat resistance, Excellent flow characteristics, Excellent adhesion to urethaneApplications: Instrument panel substrates, consoles, Cluster housing, interior trimInjection Sp.. |
|||
Tensile Strength, Yield | 98.0 MPa @Temperature 23.0 °C |
14200 psi @Temperature 73.4 °F |
ISO 527 |
Victrex® PEEK 450P Polyetheretherketone, Unreinforced Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, coarse powder for extrusion compounding, standard flow, FDA food contact comp.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | ASTM D638 |
LG Chemical LUPOY GP-5306F General Purpose PC/ABS Alloy, 30% Polymer Alloy, Weather Resistant, Flame Retardant Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO 527-1/-2 |
Lanxess Durethan® DP A 32 901510 Nylon 66 PA 66 standard injection molding grade, non-reinforced, very easy release |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp GFL14 PSU LNP* Lubricomp* GFL14 is a compound based on Polysulfone containing Glass Fiber and PTFE Lubricant.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1800E PEI Blend Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Americas re.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1810E PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Afri.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM DT1810EV PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Ultem DT1810EV PEI Blend (Europe-Africa-Middle East) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming, UL94 V0 listed.This data was supplied by SABIC-IP for.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM EXUM0167 PEI Blend Improved ductility, transparent, standard flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM EXUM0169 PEI Blend Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM EXUM0169 PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
SABIC Innovative Plastics Valox® DR48M PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® K4530 PBT (Europe-Africa-Middle East) 15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
SABIC Innovative Plastics Noryl GFN2L PPE+HIPS (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL GFN2L PPE+PS (Asia Pacific) PPE+PS GF20%, hydrolytic stability |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL HFM3015P PPE+PS (Asia Pacific) 30% GF/MF filled FR PPE/PS blend |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL NC220 PPE+HIPS (Asia Pacific) |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL CN1134 PPE+PS (Asia Pacific) 20% filled FR high modulus PPE/PS blend |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PPX ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® 20NSP Nylon 66, DAM Vydyne® 20NSP is a general-purpose, highly nucleated, lubricated PA66 resin available in natural color. It is designed to crystallize rapidly in order to reduce cycle times and increase productivit.. |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
SABIC Innovative Plastics NORYL PX2922 PPE (Asia Pacific) GF20% FR-V0 |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | SABIC - Japan Method |
SABIC Innovative Plastics Lexan® LC108 PC (Asia Pacific) Polycarbonate base, 8% carbon fiber reinforced, FR |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP JF004L PES LNP* THERMOCOMP* JF004L is a compound is based on Polyethersulfone containing 20% Glass Fiber. Characteristics of this grade is: Low Extractible |
|||
Tensile Strength, Yield | 98.0 MPa | 14200 psi | ISO 527 |
Victrex® PEEK 381G Medium Viscosity Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, depth filtered granules for specialty extrusion processes, standard flow, FD.. |
|||
Tensile Strength, Yield | 98.0 MPa @Temperature 23.0 °C |
14200 psi @Temperature 73.4 °F |
ISO 527 |
Victrex® PEEK 450G903 Black Polyetheretherketone, Unreinforced Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA food contac.. |