Polymer Property : Tensile Strength, Yield = 84.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	84.0 MPa	12200 psi	ISO value at 50 mm/min.
BASF Capron® 8202 HS BK-102 Nylon 6 (Dry) (discontinued **) Capron 8202 HS BK-102 is an unfilled, heat stabilized, pigmented black, low viscosity, general purpose nylon 6 exhibiting excellent fluidity for filling thin sections. It possesses the combination..
Tensile Strength, Yield	84.0 MPa	12200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Lubricomp KFL36XXC Acetal Copolymer (Europe-Africa-Middle East) LNP* Lubricomp* KFL36 is an Acetal containing Glass Fiber and PTFE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength, Yield	84.0 MPa	12200 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RN001S PA 66 (Asia Pacific) LNP* Lubricomp* RN001S is a compound based on Nylon 66 resin containing MOS2. Added features of this material include: Internally Lubricated, Heat Stabilized.
Tensile Strength, Yield	84.0 MPa	12200 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66 LNP* LUBRICOMP* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.
Tensile Strength, Yield	84.0 MPa	12200 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66 (Asia Pacific) LNP* Lubricomp* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated.
Tensile Strength, Yield	84.0 MPa	12200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics XenoyÂ® 1760 PBT+PC 11% Glass Reinforced PBT+PC alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors.
Tensile Strength, Yield	84.0 MPa	12200 psi	5 mm/min; ISO 527
SABIC Innovative Plastics XenoyÂ® 1760E PBT+PC 11% Glass Reinforced alloy. Impact/chemical resistant. Excellent physical property retention in automotive exteriors. High flow version of Xenoy 1760 resin.
Tensile Strength, Yield	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC (Asia Pacific) LNP* Thermocomp* DF0029ER is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant.
Tensile Strength, Yield	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP Thermocomp OF004AER PPS LNP* Thermocomp* OF004AER is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.This data was supplied by SA..
Tensile Strength, Yield	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific) LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant.
Tensile Strength, Yield	84.0 MPa	12200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP EP003 PEI LNP* Lubricomp EP003 is a Polyetherimide containing 15% PTFE/Silicone. Added features include: Internally Lubricated.
Tensile Strength, Yield	84.0 MPa	12200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Asia Pacific) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution.
Tensile Strength, Yield	84.0 MPa	12200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 9085 PEI Blend (Europe-Africa-Middle East) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 55/55 with low toxicity, smoke and flame evolution.
Tensile Strength, Yield	84.0 MPa	12200 psi	SABIC - Japan Method
SABIC Innovative Plastics XenoyÂ® 1760 PBT+PC (Asia Pacific)
Tensile Strength, Yield	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF0029ER PC LNP* Thermocomp* DF0029ER is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Mold Release, Flame Retardant.
Tensile Strength, Yield	84.0 MPa	12200 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS LNP* THERMOCOMP* ZF0049 is a compound based on PPE+PS resin containing 20% Glass Fiber. Added feature of this material is: Flame Retardant.
Tensile Strength, Yield	84.0 MPa	12200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GFN1410V PPE+PS (Europe-Africa-Middle East) Noryl* GFN1410V resin is a blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 10 % glass reinforcement. The resin is suitable for injection molding. Noryl GFN1410V resin has..
Tensile Strength, Yield	84.0 MPa	12200 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GTX GTX8408 PPE+PA Noryl GTX* GTX8408 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is glass filled and suitable for injection molding. The elongation of this material is higher than GTX8410W..
Tensile Strength, Yield	84.0 MPa	12200 psi	ASTM D6368
Solvay TECHNYLÂ® A 208KBK-10N-L PA66, DRY Description: Polyamide 66, highly UV-resistance, toughness modified for injection molding.Available in: Asia PacificProduct Applications: TECHNYL A 208K BK 10N-L is used in all sectors of industry, ..
Tensile Strength, Yield	84.0 MPa	12200 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® E51HSB NC010 Nylon 66 (Unverified Data**) Unreinforced Heat Stabilized High Viscosity Polyamide 66 Zytel E51HSB NC010 is a high molecular weight heat stabilized polyamide 66 resin for injection molding and extrusion.Information provided by ..
Tensile Strength, Yield	84.0 MPa	12200 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® E53 NC010 Nylon 66 Unreinforced High Viscosity Polyamide 66 Information provided by DuPont Performance Polymers
Tensile Strength, Yield	84.0 MPa	12200 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® EFE1068 NC010T Nylon 66 (Unverified Data**) Unreinforced Polyamide 66Zytel EFE1068 NC010T is a lubricated polyamide 66 for injection molding. It has excellent flow characteristics and was developed for fast production cycles and high producti..
Tensile Strength, Yield	84.0 MPa	12200 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® FG53 NC010 Nylon 66 (Unverified Data**) Unreinforced High Viscosity Polyamide 66 with Developed for Food Contact Applications Information provided by DuPont Performance Polymers
Tensile Strength, Yield	84.0 MPa	12200 psi	5 mm/min; ISO 527
Eurostar Starflam PX05004 PA66, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam PX05004 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
Tensile Strength, Yield	84.0 MPa	12200 psi	5 mm/min; ISO 527
Eurostar Starflam PX06010 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded Starflam PX06010 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Tensile Strength, Yield	84.0 MPa	12200 psi	50mm/min; ISO 527
BASF Ultramid® 8270 HS PA6 (Dry) Ultramid 8270 HS is a thermally modified PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile extrusion, and other applications requi..
Tensile Strength, Yield	84.0 MPa	12200 psi	2 in/min; ASTM Test
BASF Ultramid® 8270 HS PA6 (Dry) Ultramid 8270 HS is a thermally modified PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile extrusion, and other applications requi..
Tensile Strength, Yield	84.0 MPa	12200 psi	50mm/min; ISO 527
BASF Ultramid® C3U BK23079 PA66/6 (Dry) Ultramid C3U BK23079 is an injection molding, general purpose PA66/6, pigmented black grade with improved flame retardance.
Tensile Strength, Yield	84.0 MPa	12200 psi	ISO 527 type 1 A
Solvay TECHNYL® A 303 Natural FA PA66, DRY Description: Unreinforced polyamide PA66, very high viscosity, for extrusion.Available in: Europe Product Applications: TECHNYL® A 303 Natural FA offers three main advantages: high impact resistanc..
Tensile Strength, Yield	84.0 MPa	12200 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® E41HSB NC010 Nylon 66 (Unverified Data**) Unreinforced Heat Stabilized High Viscosity Polyamide 66 Zytel E41HSB is an unreinforced high viscosity heat stabilized polyamide 66 for injection molding and extrusion.Information provided by DuPon..