Polymer Property : Tensile Strength, Yield = 81900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	565 MPa @Strain 0.200 %, Temperature 650 Â°C	81900 psi @Strain 0.200 %, Temperature 1200 Â°F
Haynes 214Â® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
Haynes 214Â® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
Haynes 214Â® alloy, sheet, 32 hours exposure at 870Â°C (1600Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
Haynes 25 alloy, room temperature sheet after 1000 hours of 870Â°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	565 MPa	81900 psi	Castings
CMW® 100 Copper Alloy CMW® 100 material is a heat treatable, high strength, high conductivity copper base alloy. Its properties are a combination of highest strength and hardness with relatively high electrical and ther..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
ATI Allegheny Ludlum Stainless Steel Free Machining Grade Type 416, Tempered at 649°C (1200°F) (UNS S41600) Allegheny Ludlum's 416 is a free-machining stainless steel specifically designed to exhibit improved machinability. These modifications retain, in so far as possible, the good mechanical properties..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
Haynes Hastelloy® C-22® alloy, GMAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Tensile Strength, Yield	565 MPa	81900 psi
HP Alloys Alloy X, 5% Cold Worked 5% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, and Haynes International.