Polymer Property : Tensile Strength, Yield = 8.80 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	8.80 MPa	1280 psi	-20% change after 72 hours @ 250°C; ASTM D412
Precision Polymer Engineering V90D Fluoroelastomer Compound Fluoroelastomer Rubber, 86-93 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. Meets Aerospace Specifications DTD5612A and DTD5543B Grade 90. ASTM designation = FKM. ISO designatio..
Tensile Strength, Yield	8.80 MPa	1280 psi	-20% change after 72 hours @ 250°C; ASTM D412
Precision Polymer Engineering V90H Fluoroelastomer Compound Fluoroelastomer Rubber, 85-95 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. Formulated using only those ingredients determined by the United States Federal Food and Drug Administ..
Tensile Strength, Yield	8.80 MPa	1280 psi	ASTM D638
NOVA Chemicals Novapol® LA-0219-A LDPE Foam Resin Features: Good heat sealing latitudeModerate toughnessEasy processability Applications: Industrial packagingLinersBlends with LLDPEFoam ArticlesInformation provided by Nova Chemicals
Tensile Strength, Yield	8.80 MPa	1280 psi	ASTM D638
NOVA Chemicals Novapol® LA-0219-AM LDPE Foam Resin Good heat sealing latitude, Moderate toughness, Easy processabilityApplications: Industrial packaging, Liners, Blends with LLDPE, Foam articlesAdditives: Base resinFilm properties are typical of blo..
Tensile Strength, Yield	8.80 MPa	1280 psi	ASTM D638
NOVA Chemicals Novapol® LA-0218-AF LDPE Foam Resin (discontinued **) Good heat sealing latitude, Moderate toughness, Easy processabilityApplications: Specifically designed for foam process, Blends with LLDPEAdditives: Base resinFilm properties are typical of blown fi..
Tensile Strength, Yield	8.80 - 35.0 MPa	1280 - 5080 psi	Average value: 19.4 MPa Grade Count:34
Overview of materials for High Density Polyethylene (HDPE), Film Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Film Grade". Each property range of values reported is minimum and max..
Tensile Strength, Yield	>= 8.80 MPa	>= 1280 psi
Kazanorgsintez 108-225 Film Grade Composition of High Density Polyethylene Production Method: Based on polyethylene grades 10803-20, 15803-20, 15813-020,17504-006. Application: Designed for packing manufacture for milk and milk products.Information Provided by Kazanorg..
Tensile Strength, Yield	>= 8.80 MPa	>= 1280 psi
Kazanorgsintez 158-225 Film Grade Composition of High Density Polyethylene Production Method: Based on polyethylene grades 10803-20, 15803-20, 15813-020,17504-006. Application: Designed for packing manufacture for milk and milk products.Information Provided by Kazanorg..
Tensile Strength, Yield	>= 8.80 MPa	>= 1280 psi
Kazanorgsintez 158-76 Film Grade Composition of High Density Polyethylene Production Method: Based on polyethylene grades 10803-20, 15803-20, 15813-020,17504-006. Application: Designed for packing manufacture for milk and milk products.Information Provided by Kazanorg..
Tensile Strength, Yield	8.80 MPa	1280 psi
Dow Primacor® 3150 Ethylene Acrylic Acid (EAA) PRIMACOR® 3150 polymer containing 3% comonomer is an extrusion/ coextrusion coating and laminating for flexible packaging applications. It is designed to provide excellent adhesion to metallic, pap..
Tensile Strength, Yield	>= 8.80 MPa	>= 1280 psi
Kazanorgsintez 108-76 Film Grade Composition of High Density Polyethylene Production Method: Based on polyethylene grades 10803-20, 15803-20, 15813-020,17504-006. Application: Designed for packing manufacture for milk and milk products.Information Provided by Kazanorg..