Polymer Property : Tensile Strength, Yield = 7250 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 30.0 - 50.0 MPa
4350 - 7250 psi
Compression; ISO 527
Raschig Group 6501 DAIP
Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi..
Tensile Strength, Yield 30.0 - 50.0 MPa
4350 - 7250 psi
Compression; ISO 527
Raschig Group AMPLA® 2000 melamine-modified polyester
Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve..
Tensile Strength, Yield 30.0 - 50.0 MPa
4350 - 7250 psi
Compression; ISO 527
Raschig Group AMPLA® 2500 melamine-modified polyester
Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat..
Tensile Strength, Yield 30.0 - 50.0 MPa
4350 - 7250 psi
Compression; ISO 527
Raschig Group AMPLA® 7250 melamine-modified polyester
Cellulose reinforced melamine-modified Polyester molding compound. Very good electrical values, excellent heat resistance, excellent surface quality, low post shrinkage. This product meets the allow..
Tensile Strength, Yield 30.0 - 50.0 MPa
4350 - 7250 psi
Compression; ISO 527
Raschig Group AMPLA® 7500 melamine-modified polyester
Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta..
Tensile Strength, Yield 30.0 - 50.0 MPa
4350 - 7250 psi
Injection and Compression; ISO 527
Raschig Group EPOXIDUR® 3580 EP Epoxy
Glass-fiber reinforced and mineral filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties even with thin wall thicknesses and high temperatures. This prod..
Tensile Strength, Yield 40.0 - 50.0 MPa
5800 - 7250 psi
Compression; ISO 527
Raschig Group MELOPLAS® 150 MF
Wood flour-reinforced MF molding compound in dark colors. High surface hardness, high mechanical strength, good electrical properties. Self-extinguishing (V-O/1,6 according to UL 94), UL-listed. Fr..
Tensile Strength, Yield 42.0 - 50.0 MPa
6090 - 7250 psi
Average value: 46.6 MPa Grade Count:18
Overview of materials for PCTG Copolyester
This property data is a summary of similar materials in the MatWeb database for the category "PCTG Copolyester". Each property range of values reported is minimum and maximum values of appropriate M..
Tensile Strength, Yield 30.0 - 50.0 MPa

@Temperature 120 - 200 °C
4350 - 7250 psi

@Temperature 248 - 392 °F
Average value: 38.8 MPa Grade Count:2
Overview of materials for Nylon 46, Unreinforced
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Unreinforced". Each property range of values reported is minimum and maximum values of appropr..
Tensile Strength, Yield 39.0 - 50.0 MPa
5660 - 7250 psi
Average value: 44.8 MPa Grade Count:4
Overview of materials for Nylon 12, Graphite Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Graphite Filled". Each property range of values reported is minimum and maximum values of appr..
Tensile Strength, Yield 48.0 - 50.0 MPa
6960 - 7250 psi
ASTM D638
3D Systems Accura® 50 Plastic for SLA® Systems
Simulate the properties and appearance of molded ABS. For use with the Viper™ SLA® system, SLA 3500, SLA 5000 and SLA 7000 systems.ApplicationsFunctional components for assemblies, mock-ups and te..
Tensile Strength, Yield 34.0 - 50.0 MPa
4930 - 7250 psi
ASTM D638
Arkema Group VOLTALEF® 300 HD PCTFE
VOLTALEF® 300 HD is a chlorotrifluoroethylene powder. Used for compression molding, very good flow, non-flammable. Information provided by Arkema Group
Tensile Strength, Yield 34.0 - 50.0 MPa
4930 - 7250 psi
ASTM D638
Arkema Group VOLTALEF® 302 PCTFE
VOLTALEF® 302 is a chlorotrifluoroethylene dense powder. Used in particular for compression molding, non-flammable. Information provided by Arkema Group