Polymer Property : Tensile Strength, Yield = 7.00 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ISO 527 |
| Polimeri Europa Greenflex® MP 34 Ethylene Vinyl Acetate Copolymer - Injection Molding & Compounding Greenflex MP 34 is an ethylene vinyl acetate copolymer (EVA) for injection molding and compounding applications. Greenflex MP 34 combines high fluidity with high elasticity.Main Applications: Gree.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering F60A Fluorosilicone Rubber Blue Fluorosilicone, 56-65 °IRHD. Fluorosilicone rubber having methyl, vinyl and fluorine substituent groups on the polymer chain. To meet Aerospace Specification Mil-R-25988B, Class 1, Grade 60... |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering H80B Epichlorohydrin Peroxide Cured, Epichlorohydrin Rubber, 75-85 °IRHD. Terpolymer of epichlorohydrin, ethylene oxide and an unsaturated monomer. To ASTM D2000 line call-out: M3CH608, A25, B14, EO16, EO36, F17. AS.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering N40M Nitrile Rubber Nitrile Butadiene Rubber, 35-45 °IRHD. Medium acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene. To meet British Standard BS2751 BA40.Applications: Excellent resistance to petro.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering N65H Nitrile Rubber Nitrile Butadiene Rubber (NBR), 65-75 °IRHD. High acrylonitrile (ACN) content = 40% plus. Copolymer of acrylonitrile and butadiene.Applications: The high acrylonitrile content of this compound inc.. |
|||
| Tensile Strength, Yield | 7.00 - 13.0 MPa | 1020 - 1890 psi | ±30% change after 72 hours @ 250°C; ASTM D412 |
| Precision Polymer Engineering V71H Fluoroelastomer Compound Green Fluoroelastomer Rubber, 70-75 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. Formulated using only those ingredients determined by the United States Federal Food and Drug Ad.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 50 mm/min; ASTM D638 |
| Ovation Polymers OpteSTAT™ NC TPU 9020 Polyurethane-based Carbon Nanotube Compound Material resistivity can be tailored to the application, while retaining the physical and thermal properties of the base polymer. Applications include components of disk drives, business machines or.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | Stress at 50% Strain |
| Covestro Texin® DP 7-1158 Urethane Thermoplastic Elastomer
(discontinued **) Suitable processing methods:Injection moldingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D412 |
| Precision Polymer Engineering C90B Chloroprene Rubber Chloroprene Rubber, 86-95 °IRHD. To meet British Standard BS5176 line call-out M2BC907.Applications: A versatile rubber with good compression set properties, giving moderate resistance to petroleu.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| LyondellBasell Lupolen® V 3520 K Ethylene Vinyl Acetate Films, blow moldings.Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 20.0 % |
1020 psi @Strain 20.0 % |
DIN 53504 |
| Huntsman IROGRAN® A 95 K 4640 TPU-For Seals Introduction: IROGRAN A95K 4640 is a caprolactone-based thermoplastic polyurethane. The material has been developed for injection molding applications requiring exceptional performance in terms of c.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ASTM D638 |
| LyondellBasell Adflexâ„¢ KS-021P TPO Resin Primary Processing Method: Blown Film/Impact ModificationKey Features: excellent low temperature impact resistance, excellent chemical and environmental stress-cracking resistance, FDA acceptable, n.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp TX03476 PU LNP* Lubricomp* TX03476 is a Polyurethane containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Lubricomp TX03476 PU LNP* Lubricomp* TX03476 is a Polyurethane containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength, Yield | >= 7.00 MPa | >= 1020 psi | |
| Sibur BK-1675M Butyl Rubber (IIR) EXXON Butyl 268, PB 301 Bayer. For general and medical goods. |
|||
| Tensile Strength, Yield | >= 7.00 MPa | >= 1020 psi | |
| Sibur BK-1675N Butyl Rubber (IIR) EXXON Butyl 268, PB 301 Bayer. For production of automobile inner tubes, heating tubes, sharper vulcanizer diaphragms, and rubber fabrics. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg Commercial Neoprene® C653 Chloroprene CR or Chloroprene is a homopolymer of chloroprene or chlorobutadiene. NEOPRENE®PropertiesExcellent mechanical and abrasion properties even without reinforcing fillers.Reasonable resilience in grade.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg Hypalon® H608 Chlorosulphonated Polyethylene PropertiesExcellent resistance to oxidation and has outstanding resistance to atmospheric conditions and in particular strong sunlight and ozone.CSM compounds resist fire and are self extinguishing .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg S550 Silicone Rubber PropertiesExcellent resistance to heat (dry air), at +200°C continuous and +220°C intermittent.Remains flexible at low temperatures of -70°C.Resistant to ultra-violet light, ozone and weathering... |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg T528 Butyl Rubber Butyl rubber is a copolymer of isobutylene and a small percentage of isoprene.PropertiesWith careful compounding Butyl has really good tensile strength.Butyl has very low permeability to air and oth.. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 100 % |
1020 psi @Strain 100 % |
ISO 527-1/-2 |
| Covestro Desmopan® 786 S Polyurethane injection molding gradevery good hydrolysis and microbial resistancehigh mechanical strengthgood low-temperature flexibilityApplicationToysTechnical partsAs of 1 September 2015, Bayer MaterialScienc.. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 50.0 % |
1020 psi @Strain 50.0 % |
|
| Covestro Texin® 990 Urethane Thermoplastic Elastomer Key Features:UnfilledSuitable processing methods:Injection moldingFilm extrusionProfile extrusionSheet extrusionBlow moldingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer Mater.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 508 mm/min; ASTM D638 |
| Dow Engage® 8480 Polyolefin Elastomer Description: Engage® 8480 polyolefin elastomer is an ethyleneoctene copolymer that offers excellent performance in footwear applications and profile extrusion of tubing and hoses. It has good clari.. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 50.0 % |
1020 psi @Strain 50.0 % |
50 mm/min |
| Arkema Group Nakan® FMM 871 N PVC, Soft Injection Molding Grade NAKAN FMM 871 N is a soft polyvinyl chloride compound developed for injection molding of drip chambers for perfusion and transfusion.ISO data provided by the manufacturer, Arkema. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | ISO 527-2 |
| Arkema Group OREVAC® 18302N Maleic Anhydride Modified Linear Low Density Polyethylene OREVAC® 18365 is anhydride modified polyethylene. It is available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. OREVAC® 1.. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 50 mm/min |
| Arkema Group Evatane® 1003 VL 4C Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Thermal and colorless agricultural film to 180 at 200 µ for greenhouse coverage.ISO data provided by the .. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | 50 mm/min |
| Arkema Group Evatane® 1004 VL 4E Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Thermal and colorless agricultural film to 180 at 200 µ for greenhouse coverage.ISO data provided by the .. |
|||
| Tensile Strength, Yield | 7.00 MPa @Strain 50.0 % |
1020 psi @Strain 50.0 % |
50 mm/min |
| Arkema Group Nakan® FKS 902 R PVC, Soft Extrusion Grade NAKAN FKS 902 R is a soft polyvinyl chloride compound developed for medium voltage hard insulation.ISO data provided by the manufacturer, Arkema. |
|||
| Tensile Strength, Yield | 7.00 MPa | 1020 psi | |
| Trelleborg Commercial Neoprene® C644 Chloroprene CR or Chloroprene is a homopolymer of chloroprene or chlorobutadiene. NEOPRENE®PropertiesExcellent mechanical and abrasion properties even without reinforcing fillers.Reasonable resilience in grade.. |
|||