Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 44.1 MPa | 6400 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Rigid Extrusion 87416 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | Type I, 51 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Rigid Molding M5705 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | ASTM D638 |
Oxford Polymers OPX8320 Polybutylene Terephthalate (PBT), Impact Modified/ Glass Beads Polybutylene Terephthalate (PBT), Impact Modified/ Glass BeadsInformation provided by Oxford Polymers. |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Geon™ HTX M6215 Polyvinyl Chloride Alloy (PVC Alloy) It is recommended that the compound pellets be dried for 3 to 4 hours at 150 deg. F.Information provided by PolyOne |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | ASTM Data |
Americas Styrenics Styron® 615APR Polystyrene
(discontinued **) STYRON® 615 APR is a general purpose easy flow resin typically used for medical, pharmaceutical and thin-walled parts. It is an excellent resin for blending with K-Resin (K-Resin is a trademark of .. |
|||
Tensile Strength, Yield | 44.1 MPa @Thickness 3.20 mm |
6400 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
LG Chemical MP220 ABS, High Adhesion, Heat Resistance Feature: Injection Molding, High Adhesion, Metal PlatingApplication: Automobiles Radiator Grill, MoldingCAS No. 9003-56-9 and 9003-54-7Information provided by LG Chemical |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | ASTM D638 |
Techmer ES Plastiblend® PC/PBT IM 6200 BK Availability: North AmericaForms: PelletsAdditive: Impact ModifierFeatures: Impact ModifiedAppearance: BlackInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 44.1 MPa @Thickness 3.17 mm |
6400 psi @Thickness 0.125 in |
ASTM D638 |
Samsung Cheil Industries Starex® MP-0160RD Metal Plating Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® NH-0700FX ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® NH-0926 ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 44.1 MPa @Thickness 3.17 mm |
6400 psi @Thickness 0.125 in |
ASTM D638 |
Samsung Cheil Industries Starex® MP-0160RD Metal Plating Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® NH-0700FX ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® TX-0510 TRABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | 9.8 in/min; ASTM D638 |
Teknor Apex Sinvicomp SRP 5902 Polyvinyl Chloride, Rigid Availability: Asia Pacific Features: High Gloss; High Impact Resistance Uses: Conduit; Piping; Profiles Forms: Pellets Processing Method: ExtrusionInformation Provided by Teknor Apex |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | 9.8 in/min; ASTM D638 |
Teknor Apex Sinvicomp SRP 5906 Polyvinyl Chloride, Rigid Availability: Asia Pacific Features: Medium Impact Resistance Uses: Conduit; Piping; Profiles Forms: Pellets Processing Method: ExtrusionInformation Provided by Teknor Apex |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | ASTM 638 |
PlastxWorld CEVIAN®-V 450 ABS Heat Resistant ABSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | ASTM 638 |
PlastxWorld CEVIAN®-V 660SF ABS High Flow ABSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ABS 4107 Heat Resistant Grade Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ABS 7401 Injection Molding Grade, Extra High Impact Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ASA T-115 Description: ASA Weatherable Polymer, Injection Molding Grade, High Heat ResistanceInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 44.1 MPa @Thickness 3.20 mm |
6400 psi @Thickness 0.126 in |
Type 1, 5 mm/min speed; ASTM D-638 |
Bhansali Engineering Abstron AP-78 EP ABS Electro Plating Applications Electroplating & Hot Stamping GradesInformation provided by Bhansali |
|||
Tensile Strength, Yield | 44.1 MPa @Thickness 3.20 mm |
6400 psi @Thickness 0.126 in |
Type 1, 5 mm/min speed; ASTM D-638 |
Bhansali Engineering Abstron SE-20P ABS Sheet Extrusion Grade ABS Pipe GradeInformation provided by Bhansali |
|||
Tensile Strength, Yield | 44.1 MPa @Thickness 3.20 mm |
6400 psi @Thickness 0.126 in |
Type 1, 5 mm/min speed; ASTM D-638 |
Bhansali Engineering Abstron SE-22 ABS Sheet Extrusion Grade Sheet Extrusion grade for profile & DoorsInformation provided by Bhansali |
|||
Tensile Strength, Yield | 44.1 MPa @Thickness 3.20 mm |
6400 psi @Thickness 0.126 in |
Type 1; ASTM D638 |
Bhansali Engineering Abstron IM-29 ABS Injection Molding Grade High Impact, Medium, High Flow, General PurposeInformation provided by Bhansali |
|||
Tensile Strength, Yield | 44.1 MPa @Thickness 3.20 mm |
6400 psi @Thickness 0.126 in |
Type 1, 5 mm/min speed; ASTM D-638 |
Bhansali Engineering Abstron SE-22 ABS Sheet Extrusion Grade Sheet Extrusion grade for profile & DoorsInformation provided by Bhansali |
|||
Tensile Strength, Yield | 44.1 MPa @Thickness 3.20 mm |
6400 psi @Thickness 0.126 in |
Type 1, 5 mm/min; ASTM D-638 |
Bhansali Engineering Abstron KU-650M ABS Super Heat Resistant High Heat Resistant Grades with Better Flow characteristicInformation provided by Bhansali |
|||
Tensile Strength, Yield | 44.1 MPa @Thickness 3.20 mm |
6400 psi @Thickness 0.126 in |
Type 1; ASTM D638 |
Bhansali Engineering Abstron MIF-35 ABS Injection Molding Grade High Impact, Medium, High Flow, General PurposeInformation provided by Bhansali |
|||
Tensile Strength, Yield | 44.1 MPa | 6400 psi | ASTM D638 |
Polymer Resources PC/TP-GP3 PC Polyester, High Impact, Superior Chemical Resistance
(Unverified Data**)&l Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |