Polymer Property : Tensile Strength, Yield = 63800 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	440 MPa @Strain 0.200 %	63800 psi @Strain 0.200 %
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175Â°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Yield	440 MPa @Strain 0.200 %	63800 psi @Strain 0.200 %
Haynes 188 alloy, plate at RT after 16000 hours at 870Â°C (1600Â°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095Â°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Yield	440 MPa @Strain 0.200 %	63800 psi @Strain 0.200 %
Haynes 230Â® alloy plate, 1000 hours exposure at 649Â°C (1200Â°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149Â°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Yield	440 MPa @Strain 0.200 %	63800 psi @Strain 0.200 %
Haynes 625 alloy, plate after 8000 hours at 870Â°C (1600Â°F) Cb and Ta content 3.7% combined. Excellent strength up to 816Â°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Yield	440 MPa	63800 psi
Superior Die Set FORTALÂ® HP Aluminum Alloy Description: FORTAL is a high strength, lightweight, easy to machine alloy, originally developed to be used in the aerospace industry. It can be found whenever a structure is highly solicited and d..
Tensile Strength, Yield	440 MPa @Temperature 24.0 °C	63800 psi @Temperature 75.2 °F	Warp TS
Hexcel® HexPly® F185 Epoxy Resin, 7781 Glass Fabric Hexcel designation: 7781-38"-F185; Fiber: 75-1/0Information provided by HexCel
Tensile Strength, Yield	440 - 490 MPa	63800 - 71100 psi	L direction
ArcelorMittal Speed 35-440 Electrical Steel Properties: The iCARe™ Speed product family comes with guaranted losses at 400Hz and indicative maximum values at 700Hz. These values are representative of the steel’s behaviour at high frequencie..
Tensile Strength, Yield	440 MPa	63800 psi	Typical
ATI Allegheny Ludlum AL 601™ Nickel-Base Alloy, Annealed at 982°C (1800°F), UNS N06601 Allegheny Ludlum's AL 601 alloy is an austenitic nickel-chromium-iron alloy designed for both heat and corrosion resistance. As compared to AL 600 alloy, the AL 601 alloy has, in addition to increa..
Tensile Strength, Yield	>= 440 MPa	>= 63800 psi	35<x=50mm
ThyssenKrupp XABO® 460 Structural Steel This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-..
Tensile Strength, Yield	440 MPa @Strain 0.200 %	63800 psi @Strain 0.200 %
Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Yield	>= 440 MPa	>= 63800 psi	35<x=50mm
ThyssenKrupp XABO® 460 T Structural Steel This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-..