Polymer Property : Tensile Strength, Yield = 565 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	565 MPa @Strain 0.200 %, Temperature 650 Â°C	81900 psi @Strain 0.200 %, Temperature 1200 Â°F
Haynes 214Â® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
Haynes 214Â® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
Haynes 214Â® alloy, sheet, 32 hours exposure at 870Â°C (1600Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
Haynes 25 alloy, room temperature sheet after 1000 hours of 870Â°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Yield	565 MPa	82000 psi
Universal Wire Works 622 Nickel Alloy Welding Wire Alloy 622 is an alloy of nickel with chromium, molybdenum, tungsten as principal alloying elements. It is used to weld alloys of similar composition as well as dissimilar joints between nickel-chrom..
Tensile Strength, Yield	565 - 627 MPa	82000 - 91000 psi	0.2% offset
Eagle Brass 260 Cartridge Brass, Spring Alloy C260 is commonly used for electrical components, electronic parts, and mechanical fasteners. The alloy has good strength but poor stress relaxation characteristics and does not make a particul..
Tensile Strength, Yield	565 - 710 MPa	82000 - 103000 psi	0.2% offset
Eagle Brass 762 Nickel Silver 12%, Hard 762 is a nickel silver alloy that has excellent strength, stress relaxation resistance, and solderability. Due to it being extremely resistant to corrosion it doesn't tarnish easily and has a long s..
Tensile Strength, Yield	565 MPa	81900 psi	Castings
CMW® 100 Copper Alloy CMW® 100 material is a heat treatable, high strength, high conductivity copper base alloy. Its properties are a combination of highest strength and hardness with relatively high electrical and ther..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
ATI Allegheny Ludlum Stainless Steel Free Machining Grade Type 416, Tempered at 649°C (1200°F) (UNS S41600) Allegheny Ludlum's 416 is a free-machining stainless steel specifically designed to exhibit improved machinability. These modifications retain, in so far as possible, the good mechanical properties..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi..
Tensile Strength, Yield	565 MPa @Strain 0.200 %	81900 psi @Strain 0.200 %
Haynes Hastelloy® C-22® alloy, GMAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..
Tensile Strength, Yield	565 MPa	81900 psi
HP Alloys Alloy X, 5% Cold Worked 5% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, and Haynes International.