Polymer Property : Tensile Strength, Yield = 555 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 555 MPa

@Strain 0.200 %,
Temperature 316 °C
80500 psi

@Strain 0.200 %,
Temperature 600 °F
Kennametal Stellite Stellite® 6K 12.7 or 22.2 mm plate
13.3 mm^3 volume loss--abrasive wear data. Applications include agitators, augers, ball mills, banbury mills, cams, crusher bearings, dryers, dry presses, dump cars, fans, filters, food machinery, g..
Tensile Strength, Yield 555 MPa

@Strain 0.200 %
80500 psi

@Strain 0.200 %
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes
Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr..
Tensile Strength, Yield 555 MPa

@Strain 0.200 %
80500 psi

@Strain 0.200 %
Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Yield 555 MPa

@Strain 0.200 %
80500 psi

@Strain 0.200 %
Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic..
Tensile Strength, Yield 555 MPa
80500 psi
Haynes Hastelloy® W alloy, gas metal arc welds, as-welded
Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica..
Tensile Strength, Yield 555 MPa
80500 psi
Haynes Hastelloy® W alloy, gas tungsten arc welds, as-welded
Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica..
Tensile Strength, Yield 555 MPa

@Strain 0.200 %,
Temperature 425 °C
80500 psi

@Strain 0.200 %,
Temperature 797 °F
Haynes 242® alloy, hot rolled plate, annealed and aged
Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good thermal..
Tensile Strength, Yield 555 MPa

@Strain 0.200 %
80500 psi

@Strain 0.200 %
Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..