Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	34.8 MPa	5050 psi	ASTM D638
RedEye On Demand PC/ABS for FDM Rapid Prototyping This thermoplastic polymer blend combines PC (Polycarbonate) and ABS (Acrylonitrile Butadiene Styrene) to produce an industrial material with a lot to offer. It combines the strength of PC with the ..
Tensile Strength, Yield	34.8 - 119 MPa	5050 - 17300 psi	Average value: 56.6 MPa Grade Count:724
Overview of materials for Polycarbonate/ABS Alloy, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, Unreinforced". Each property range of values reported is minimum and maximum va..
Tensile Strength, Yield	34.8 MPa	5050 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 287ºF Cure Temperature MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	34.8 MPa	5050 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 5 Minutes Milling MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	34.8 MPa	5050 psi	(2 in/min); ASTM D638
Phillips 66 COPYLENE® CR030LN Polypropylene, Mini-Random Copolymer, Thermoforming COPYLENE™ CR030LN is a mini-random copolymer with a high performance nucleation system designed to yield high clarity thermoformed articles.Applications: ThermoformingInformation provided by Philli..
Tensile Strength, Yield	34.8 MPa	5050 psi	ASTM D638
Washington Penn Homopolymer Polypropylene 10% Talc Filled Talc-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug packaging requi..
Tensile Strength, Yield	34.8 MPa	5050 psi	ASTM D638
Washington Penn Homopolymer Polypropylene 20% Talc Filled Talc-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug packaging requi..
Tensile Strength, Yield	34.8 MPa	5050 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 287ºF Cure Temperature MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	34.8 MPa	5050 psi	83% Ret.
UBE UBESTA® 3030U Nylon 12 (After Sulfuric Acid (10%) for 500 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c..
Tensile Strength, Yield	34.8 MPa	5050 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 5 Minutes Milling MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	34.8 MPa	5050 psi	chs 2 in/min; ASTM D638
Diamond Polymers ASA TWP 502 Description: Transparent Weatherable PolymerInformation provided by Diamond Polymers, Inc.
Tensile Strength, Yield	34.8 MPa	5050 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N330 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	34.8 MPa	5050 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N330 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	34.8 MPa	5050 psi	2 in/min; ASTM D638
Phillips 66 COPYLENE® CH008 Polypropylene, Homopolymer, Netting COPYLENE™ CH008 is a fractional melt flow polypropylene homopolymer resin available in pellet form. Applications: Raffia/Tapes/Strapping; Anti-Corrosion Coating; Geotextile & Agriculture; Nets. Rep..