Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 345 MPa | 50000 psi | |
Pacific Sintered Materials FX-227-T Infiltrated Steel Powdered Metal Machines and plates well. Good in hydraulic applications. Moderate tolerance control.Equivalent MPIF Specification: FX-1005-50All information provided by Pacific Sintered Metals. |
|||
Tensile Strength, Yield | 345 MPa | 50000 psi | |
Materion BrushBronze® 630 (AMS 4640) 3.0" - 5.0" Information supplied by Brush Wellman Engineered Materials.BrushBronze™ 630 is an Aluminum-Nickel-Bronze alloy that combines high strength along with resistance to wear under severe loading con.. |
|||
Tensile Strength, Yield | 345 - 414 MPa @Strain 0.200 % |
50000 - 60000 psi @Strain 0.200 % |
|
Materion BrushCAST® 275C High Strength Casting Alloy (As Cast) Pouring Temperature: 960-1035°CHeat treatment required for max strength (Annealing): 760-790°C/water quenchHeat treatment required for max strength (Hardening): 760-790°C/water quenchDescri.. |
|||
Tensile Strength, Yield | 345 - 448 MPa | 50000 - 65000 psi | |
Meehanite Almanite® WS Wear and Abrasion Resisting Cast Iron Type WS is a hard wearing martensitic iron with exceptional impact strength...not readily machinable...work hardens in service to high hardness values. Type WS is recommended for crusher jaws, impa.. |
|||
Tensile Strength, Yield | >= 345 MPa | >= 50000 psi | |
MetalTek C18100 Chrome Zirc Copper High Conductivity Typical property data from forged samples.Information provided by MetalTekCast UNS C18100; Cast Grade C18100 |
|||
Tensile Strength, Yield | >= 345 MPa | >= 50000 psi | |
MetalTek MTEK 175-B Cast UNS C95410 Aluminum Bronze Versatile alloy with high strength, good ductility, unusual toughness, plus exceptional wear resistance. Aluminum Bronze heat treated to higher mechanical properties where necessary.Information prov.. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 %, Temperature 870 °C |
50000 psi @Strain 0.200 %, Temperature 1600 °F |
|
Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 %, Temperature 870 °C |
50000 psi @Strain 0.200 %, Temperature 1600 °F |
|
Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | >= 345 MPa | >= 50000 psi | |
MetalTek MTEK 275 Cast UNS C95900 Aluminum Bronze Engineered alloy for excellent wear and anti-galling properties in forming, bending and drawing dies. Aluminum Bronze heat treated to higher mechanical properties where necessary.Information provide.. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 %, Temperature 260 °C |
50000 psi @Strain 0.200 %, Temperature 500 °F |
|
Haynes Hastelloy® G-30® alloy, all-weld metal, GMAW weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 % |
50000 psi @Strain 0.200 % |
Sheet |
Special Metals INCONEL® HX Nickel Superalloy Data provided by the manufacturer, Special Metals. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 % |
50000 psi @Strain 0.200 % |
Typical |
TIMET TIMETAL® 50A CP Titanium (ASTM Grade 2) Commercially Pure Titanium.Industry Specifications: USA Aerospace: AMS 4902, 4941. Germany Engineering: 3.7035. Germany Aerospace: 3.7034. France: T-40. UK Aerospace Specifications BS TA. 2, 3,.. |
|||
Tensile Strength, Yield | >= 345 MPa | >= 50000 psi | 0.2% offset |
Eagle Brass 19010 XP-150 Copper Nickel Silicon, 3/4 Hard 19010 is an extreme versatile high performance copper nickel silicon alloy. It has an excellent combination of strength, conductivity and formability. Typical uses include terminals, relays, connect.. |
|||
Tensile Strength, Yield | 345 - 427 MPa | 50000 - 62000 psi | 0.2% offset |
Eagle Brass 19210 XP-10 Copper Iron, 3/4 Hard 19210 has higher strengths than most copper alloys but thanks to its composition and processing it retains formability and conductivity that other copper alloys lose. Typical uses include cooling f.. |
|||
Tensile Strength, Yield | 345 MPa | 50000 psi | |
CMW® DSC Copper with Dispersed Aluminum Oxide CMW® DSC material is an extruded and cold worked powder metallurgy material consisting of copper and dispersed aluminum oxide. It has exceptional high temperature strength for its electrical conduc.. |
|||
Tensile Strength, Yield | 345 MPa | 50000 psi | Typical |
Dura-Bar 65-45-12 Continuously Cast Ductile Iron Bar Stock ASTM A536 Continuously cast ductile iron bar stock is produced in a wide variety of sizes and shapes, including rounds, rectangles and special shape cross sections.It often is used as a direct replacement for.. |
|||
Tensile Strength, Yield | 345 MPa | 50000 psi | Annealed |
California Fine Wire Dumet Nickel Iron Core Copper Clad Alloy All values may vary dependent on specific design and usage99.9% copper cladding over iron-nickel coreCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Tensile Strength, Yield | 345 MPa | 50000 psi | Annealed |
California Fine Wire Permanickel® K-300 Nickel Alloy All values may vary dependent on specific design and usagePermanickel® is a registered trade name of the Inco family of products.Capabilities: WireRibbonInsulatedPlatedInformation provided by Calif.. |
|||
Tensile Strength, Yield | 345 - 372 MPa @Strain 0.200 %, Thickness 1.02 mm |
50000 - 54000 psi @Strain 0.200 %, Thickness 0.0402 in |
|
AK Steel 11 Cr-Cb™ Ferritic Stainless steel AK Steel 11 Cr-Cb™ has increased silicon levels and is dual stabilized with titanium and columbium. Designed for use in automotive exhaust tubing and other high-temperature applications, this is a.. |
|||
Tensile Strength, Yield | 345 MPa | 50000 psi | In rolling direction |
AK Steel TRAN-COR® H-0 CARLITE® Grain Oriented Electrical Steel TRAN-COR H CARLITE® high permeability electrical steels offer an outstanding degree of grain orientation, This combination of higher permeability with low residual stress offers the potential for l.. |
|||
Tensile Strength, Yield | 345 MPa | 50000 psi | In rolling direction |
AK Steel TRAN-COR® H-2 CARLITE® Grain Oriented Electrical Steel TRAN-COR H CARLITE® high permeability electrical steels offer an outstanding degree of grain orientation, This combination of higher permeability with low residual stress offers the potential for l.. |
|||
Tensile Strength, Yield | 345 MPa | 50000 psi | |
Carpenter Kovar® Alloy (Glass and Ceramic Sealing Alloy) Data provided by Carpenter Technology Corporation.Kovar® alloy is a vacuum melted, Fe-Ni-Co, low expansion alloy whose chemical composition is controlled within narrow limits to assure precise unif.. |
|||
Tensile Strength, Yield | >= 345 MPa | >= 50000 psi | |
AK Steel ZINCGRIP® FORMABLE 50K / ASTM A1008 class 2 / SAE J1392 050 XLK, Grade 50 Electrogalvanized Carbon Steel, High Strength Low Alloy Steel (HSLAS) Information provided by AK Steel |
|||
Tensile Strength, Yield | 345 - 517 MPa @Strain 0.200 % |
50000 - 75000 psi @Strain 0.200 % |
|
Ametek High Purity Nickel Strip 899A 1/2 Hard Information supplied by Ametek Specialty Metal Products.AMETEK High Purity Nickel offers major advantages to the rechargeable battery industry, including:Lowest electrical resistivity available in p.. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 % |
50000 psi @Strain 0.200 % |
Typical; Annealed Plate |
ATI Allegheny Ludlum AL 22™ Nickel-Base Alloy, UNS N06022 AL 22 alloy is a Ni-Cr-Mo alloy that provides outstanding resistance to pitting, crevice corrosion, intergranular attack, and stress corrosion cracking. The combination of Cr, Ni, Mo, and W provide.. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 % |
50000 psi @Strain 0.200 % |
|
ATI Allvac® AL 6XN® UNS N08367 Specialty Steel Uses: Process equipment, flue-gas scrubber systems, multi-effect evaporators for brines, seawater, pulp & paper liquors.Property values are for samples in the metallurgical condition: 2050°F anneal.. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 % |
50000 psi @Strain 0.200 % |
|
ATI Allvac® M-252 Nickel Superalloy, Heat Treatment: 1177°C (2150°F) Anneal Applications: Turbine blades, fasteners, and high temperature bolting.Data provided by Allvac. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 % |
50000 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum Grade 2 Titanium (UNS R50400) Uses: CPI equipment, industrial components, condenser tubing.Mechanical property data below is typical of annealed samples at room temperature.Information provided by Allegheny Ludlum. |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 % |
50000 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum AL 17-7™ High Strength Stainless Steel, UNS S17700 Property data below is typical of annealed samples. Available in sheet and strip. For use in high-strength springs, bellows, and aerospace applications.Information provided by Allegheny Ludlum |
|||
Tensile Strength, Yield | 345 MPa @Strain 0.200 % |
50000 psi @Strain 0.200 % |
|
ATI Allegheny Ludlum Grade 7 Titanium (UNS R52400) Uses: CPI equipment, industrial components, tubing.Mechanical property data below is typical of annealed samples at room temperature.Information provided by Allegheny Ludlum. |