Polymer Property : Tensile Strength, Yield = 5.50 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 5.50 MPa
798 psi
200%, post cured- 4 hours at 166°C; ASTM D412
Multibase SILASTIC® 7-6860 Dow-Corning Biomedical Grade Liquid Silicone Rubber
Information provided by Multibase
Tensile Strength, Yield 5.50 MPa
798 psi
ASTM D412
Polymax® Maxelast® P3650 TPE, PP Overmold or Standalone use
Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsTool Hand GripsSporting GoodsWire & Cable ElectronicsMedical DevicesPlasti..
Tensile Strength, Yield 5.50 MPa
798 psi
ASTM D412
Precision Polymer Engineering F70R Fluorosilicone Rubber
Red Fluorosilicone, 65-75 °IRHD. Fluorosilicone rubber having methyl, vinyl and fluorine substituent groups on the polymer chain. To meet Aerospace Specification DTD5583A Grade 70.Applications: S..
Tensile Strength, Yield 5.50 MPa
798 psi
ASTM D412
Precision Polymer Engineering S70N Silicone Rubber
Silicone Rubber, 66-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. To meet UK Ministry of Defence Aircraft Materials Specification DTD5582A Grade ..
Tensile Strength, Yield 5.50 MPa
798 psi
ASTM D412
Precision Polymer Engineering S80N Silicone Rubber
Silicone Rubber, 76-85 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. To meet UK Ministry of Defence Aircraft Materials Specification DTD5582A Grade ..
Tensile Strength, Yield 5.50 MPa
798 psi
M100
3M Dyneon™ Fluorel™ FE-5610Q Fluoroelastomer VF2 + HFP Dipolymer  (discontinued **)
Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the c..
Tensile Strength, Yield 5.50 MPa
798 psi
M100
3M Dyneon™ Fluorel™ FT-2481 Fluoroelastomer VF2 + HFP Dipolymer  (discontinued **)
Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 68.6%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, 4% Ca(OH)2, 1.4% Dihydroxy Crosslinker, 0.4% Phosp..
Tensile Strength, Yield 5.50 MPa
798 psi
Kraton® D1102 + LDPE blend (50/50)
Blending KRATON D and G polymers with PE significantly improves the toughness at both room and low temperatures. KRATON polymers are block segments of styrene and rubber monomers (A-B, A-B-A, or [A..
Tensile Strength, Yield 5.50 MPa
798 psi
Elastic; ASTM D412
Multibase Multi-Flex® A 4001 LC Black TPE Thermoplastic Elastomer
Features: Heat Resistance, HighOzone ResistantCompression Set, Low Forms: PelletsProcessing Method:Injection Molding Information provided by Multibase
Tensile Strength, Yield 5.50 MPa
798 psi
chs 2.0 in/min; ASTM D638
Diamond Polymers Softflex® 2701-1502R
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Tensile Strength, Yield 5.50 MPa
798 psi
chs 2.0 in/min; ASTM D638
Diamond Polymers Softflex® SF 5060 Overmold for Nylon
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Tensile Strength, Yield 5.50 MPa
798 psi
chs 20 in/min; ASTM D638
Diamond Polymers Softflex® SF 8900
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Tensile Strength, Yield 5.50 MPa
798 psi
Film Property, 50 µm thickness; ASTM D882
Arkema Group OREVAC® 9314 EVA Terpolymer
OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre..
Tensile Strength, Yield 5.50 MPa
798 psi
cured 72 hrs @ RT
ACC QM 264 QSI Quantum Silicones 60 Durometer Addition Cure Moldmaking Material
QM 264 is a two component, room temperature addition cure silicone material. The cured rubber has excellent mechanical properties, good shelf-life stability, excellent physical properties and resin ..
Tensile Strength, Yield 5.50 MPa
798 psi
50 mm/min
Arkema Group Evatane® 1005 VN 4 Ethylene Vinyl Acetate
EVA copolymer made by high pressure tubular process. Applications Grade for flexible films with high transparency and very high mechanical properties. Examples: high strength stretch film, greenhous..