Polymer Property : Tensile Strength, Yield = 4650 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	32.1 MPa	4650 psi	2 in/min; ASTM D638
Phillips 66 COPYLENE® CR027 Polypropylene, Homopolymer, Mini-random, BOPP Mini-random homopolymer. Applications: BOPP film. Equivalent to Pro-fax® HL456JInformation provided by Phillips 66.
Tensile Strength, Yield	32.1 MPa	4650 psi	ASTM D882
Formosa Plastics Formolene® LH6008 Injection Molding HDPE (discontinued **) HomopolymerApplications: Totes, cases, crates, over-caps, toysFormolene LH6008 is a high density polyethylene for injection molding applications.Meets all requirements of the U.S. Food and Drug Admi..
Tensile Strength, Yield	32.1 MPa	4650 psi	ASTM D882
Formosa Plastics Formolene® LH6008U Injection Molding HDPE (discontinued **) HomopolymerApplications: Totes, cases, crates, over-caps, toysFormolene LH6008U is a high density polyethylene for injection molding applications with UV stabilizer.Meets all requirements of the U.S..
Tensile Strength, Yield	32.1 MPa	4650 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N339 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	32.1 MPa	4650 psi	2 in/min; ASTM D638
Phillips 66 COPYLENE® CH042L Polypropylene, Homopolymer, Straw and Extrusion, Antistat COPYLENE™ CH042L is specifically designed for application in extrusion applications such as straws. Applications: Straws.Information provided by Phillips 66.
Tensile Strength, Yield	32.1 MPa	4650 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N339 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	32.1 MPa	4650 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N220 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	32.1 MPa	4650 psi	2" per min, Type IV; ASTM D638
Amco PRIMATOP HDPE 080960 Injection Molding Polyethylene HDPE 080960 features high stiffness, maximum toughness, good top loading capability, and high surface gloss. Applications include tote boxes and beverage crates.Former A-Top Polymers product; part o..
Tensile Strength, Yield	32.1 MPa	4650 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N220 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	32.1 MPa	4650 psi	50 mm/min; ASTM D638
Amco PRIMATOP PP CO 350-10 RC Clarified Random Copolymer Features:excellent processingimpactclarityanti-statApplications:rigid packaginghousewaresFormer A-Top Polymers product; part of Amco product line since 2013.