Polymer Property : Tensile Strength, Yield = 38.2 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 38.2 MPa
5550 psi
ASTM D638
PolyMirae Moplen HP640G Sheet and Thermoforming Grade Polypropylene
Moplen HP640G is the polypropylene Homopolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen HP640G is a homopolymer particularly suitable for sheet and thermof..
Tensile Strength, Yield 38.2 MPa
5540 psi
Type I, 5.1 mm/min; ASTM D638
PolyOne Geon™ Vinyl Dry Blend E6001 Polyvinyl Chloride, Rigid (PVC, Rigid)
Information provided by PolyOne
Tensile Strength, Yield 38.2 MPa

@Thickness 3.20 mm
5550 psi

@Thickness 0.126 in
50 mm/min; ASTM D638
LG Chemical HI100H ABS, High Impact, High Toughness
Feature: Injection Molding, High Impact, High ToughnessApplication: Helmet, Pipe & Fittings)CAS No. 9003-56-9Information provided by LG Chemical
Tensile Strength, Yield 38.2 MPa

@Thickness 3.20 mm
5550 psi

@Thickness 0.126 in
50 mm/min; ASTM D638
LG Chemical HI100K ABS, High Impact
Feature: Injection Molding, High Impact, Good ProcessingApplication: Miscellaneous Goods)CAS No. 9003-56-9Information provided by LG Chemical
Tensile Strength, Yield 38.2 MPa

@Thickness 3.20 mm
5550 psi

@Thickness 0.126 in
50 mm/min; ASTM D638
LG Chemical RX710 ABS, High Impact, Chemical Resistance to HCFC
Feature: Injection Molding, Chemical Resistance to HCFC, High ImpactApplication: Refrigerator Dispensor & HomebarCAS No. 9003-56-9Information provided by LG Chemical
Tensile Strength, Yield 38.2 MPa
5540 psi
ASTM D638
Lotte Chemical Titan TITANPRO® PM430 Polypropylene homopolymer
Titanpro® PM430 is designed without any slip agents nor antiblocking agents. The base resin meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520(a)(1)(..
Tensile Strength, Yield 38.2 MPa
5550 psi
50 mm/min; ASTM D638
Samsung Cheil Industries Starex® EG-7000 ABS/PET, Unreinforced
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 38.2 MPa
5550 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Starex® NA-0660I ABS, Unreinforced Anti-Bacteria Grade
Nano-silver high flowability antibacterial ABS that can be used in notebook keyboardsInformation provided by Samsung Cheil Industries.
Tensile Strength, Yield 38.2 MPa
5550 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Starex® SP-0170 ABS, Unreinforced Extrusion Grade
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 38.2 MPa
5550 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Starex® WR-9130 ASA, Unreinforced
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 38.2 MPa
5550 psi
50 mm/min; ASTM D638
Samsung Cheil Industries Starex® EG-7000 ABS/PET, Unreinforced
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 38.2 MPa
5550 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Starex® NA-0660I ABS, Unreinforced Anti-Bacteria Grade
Nano-silver high flowability antibacterial ABS that can be used in notebook keyboardsInformation provided by Samsung Cheil Industries.
Tensile Strength, Yield 38.2 MPa
5550 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Starex® SP-0170 ABS, Unreinforced Extrusion Grade
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 38.2 MPa
5550 psi
5 mm/min; ASTM D638
Samsung Cheil Industries Starex® WR-9130 ASA, Unreinforced
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 38.2 MPa
5550 psi
ASTM D638
SCG Chemicals EL-Leneâ„¢ H5480S High Density Polyethylene Monofilament
Key Characteristics:High tenacityExcellent product colorRecommended Applications: Monofilament and flat yarn extrusion for manufacturing of nets, ropes and tarpaulinInformation provided by SCG Chem..
Tensile Strength, Yield 38.2 MPa
5550 psi
at 300% elongation; ASTM D412
Lubrizol Estane® S364D Thermoplastic Polyurethane
Type: Estane® S364D is a Shore 65D, polyester based thermoplastic polyurethane (TPU) with excellent transparency. FDA approved (21 CFR 177.2600, 177.1680).Uses: Injection Molding.Availability: Asi..
Tensile Strength, Yield 38.2 MPa
5550 psi
at 300% elongation; ASTM D412
Lubrizol Estane® S368D Thermoplastic Polyurethane
Type: Estane® S368D is a Shore 68D, polyester based thermoplastic polyurethane (TPU) with excellent transparency. FDA approved (21 CFR 177.2600, 177.1680).Uses: Injection Molding.Availability: Asi..
Tensile Strength, Yield 38.2 MPa

@Thickness 3.20 mm
5550 psi

@Thickness 0.126 in
Type 1, 5 mm/min speed; ASTM D-638
Bhansali Engineering Abstron TG-3(M) ABS High Impact Injection Molding
Very High & Medium Impact, Paintable Automotive Grades Information provided by Bhansali
Tensile Strength, Yield 38.2 MPa

@Thickness 3.20 mm
5550 psi

@Thickness 0.126 in
Type 1, 5 mm/min speed; ASTM D-638
Bhansali Engineering Abstron HI-34 ABS High Impact Injection Molding
Very High & Medium Impact, Paintable Automotive Grades Information provided by Bhansali
Tensile Strength, Yield 38.2 MPa

@Thickness 3.20 mm
5550 psi

@Thickness 0.126 in
Type 1; 5mm/min speed; ASTM D638
Bhansali Engineering Abstron SE-45 ABS Sheet Extrusion Grade
Super high and Very High Impact Sheeting grades for Automobile & Luggage ApplicationsInformation provided by Bhansali
Tensile Strength, Yield 38.2 MPa

@Thickness 3.20 mm
5550 psi

@Thickness 0.126 in
Type 1, 5 mm/min speed; ASTM D-638
Bhansali Engineering Abstron TG-3(M) ABS High Impact Injection Molding
Very High & Medium Impact, Paintable Automotive Grades Information provided by Bhansali
Tensile Strength, Yield 38.2 MPa

@Thickness 3.20 mm
5550 psi

@Thickness 0.126 in
Type 1, 5 mm/min speed; ASTM D-638
Bhansali Engineering Abstron HI-34 ABS High Impact Injection Molding
Very High & Medium Impact, Paintable Automotive Grades Information provided by Bhansali
Tensile Strength, Yield 38.2 MPa

@Thickness 3.20 mm
5550 psi

@Thickness 0.126 in
Type 1, 5 mm/min speed; ASTM D-638
Bhansali Engineering Abstron PT-45M ABS Antistatic Extrusion Grade
Antistatic Cop Sleeves ApplicationInformation provided by Bhansali
Tensile Strength, Yield 38.2 MPa

@Thickness 3.20 mm
5550 psi

@Thickness 0.126 in
Type 1, 5 mm/min speed; ASTM D-638
Bhansali Engineering Abstron PT-45M ABS Antistatic Extrusion Grade
Antistatic Cop Sleeves ApplicationInformation provided by Bhansali
Tensile Strength, Yield 38.2 MPa
5550 psi
ASTM D638
Cheng Yu Plastic BK1021 Electric Conducting Polypropylene, Extrusion
Tensile Strength, Yield 38.2 MPa

@Thickness 3.20 mm
5550 psi

@Thickness 0.126 in
Type 1; 5mm/min speed; ASTM D638
Bhansali Engineering Abstron SE-45 ABS Sheet Extrusion Grade
Super high and Very High Impact Sheeting grades for Automobile & Luggage ApplicationsInformation provided by Bhansali