Polymer Property : Tensile Strength, Yield = 35.8 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 35.8 MPa
5190 psi
Type I, 5.1 mm/min; ASTM D638
PolyOne Geon™ HTX Ultra LA426G Black 2880 Polyvinyl Chloride Alloy (PVC Alloy)
Higher gloss version of Geon HTX Ultra LA426Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Physical properties measured on LA426G Black 2880.Information provided by Pol..
Tensile Strength, Yield 35.8 MPa
5190 psi
Ineos ABS Lustran® LGM
Key Features:UnfilledSuitable processing methods:Injection molding
Tensile Strength, Yield 35.8 MPa
5190 psi
2 in/min (50 mm/min); ASTM D-638
Ineos H00G-00 Polypropylene Homopolymer
A polypropylene homopolymer produced by Ineos utilizing catalyst technology. This material meets the Food and Drug Administration requirements of 21CFR 177.1520. Homopolymer H00G-00 meets certain ..
Tensile Strength, Yield 35.8 MPa
5190 psi
ASTM D638
IRPC Polimaxx Polene 1111NX TA8 Polypropylene Compound
CHARACTERISTICS: POLYPROPYLENE HOMOPOLYMER WITH 40% TALCUM REINFORCED HIGH STIFFNESSAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES
Tensile Strength, Yield 35.8 MPa
5190 psi
ASTM D638
A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene
DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible..
Tensile Strength, Yield 35.8 MPa
5190 psi
ASTM D638
A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene
DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible..
Tensile Strength, Yield 35.8 MPa
5190 psi
ASTM D638
A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene
DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible..
Tensile Strength, Yield 35.8 MPa
5190 psi
ASTM D638
A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene
DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible..
Tensile Strength, Yield 35.8 MPa
5190 psi
Elastic Limit
Wolf Kunststoff ZEDEX® ZX-750V5T A9T Polymer Alloy
Main Characteristics: Hard; Stiff; Tough; High dimensional stability; High fatigue strength; High weather resistance; Good fire behavior; Suitable for vacuum; Good machinability; Contains PTFE; Stre..
Tensile Strength, Yield 35.8 MPa
5190 psi
ASTM D638
A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene
DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible..
Tensile Strength, Yield 35.8 MPa
5190 psi
chs 2 in/min; ASTM D638
Diamond Polymers Diamaloy ABS VP-22 Flame Retardant ABS
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Tensile Strength, Yield 35.8 MPa
5190 psi
chs 2.0 in/min; ASTM D638
Diamond Polymers DIAMALOY VP22 Flame Retardant ABS
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Tensile Strength, Yield 35.8 MPa
5190 psi
chs 2.0 in/min; ASTM D638
Diamond Polymers DIAMALOY VP22 NATURAL 1001B Blow Molding Grade, Flame Retardant ABS
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Tensile Strength, Yield 35.8 MPa
5190 psi
ASTM D638
A. Schulman POLYFORT™ PP 2801 Homopolymer Polypropylene
DescriptionPolyfort® PP 2801 is a 12 melt flow homopolymer polypropylene based on the same ingredients as Eastman P4G4Z-001. It is compounded on equipment and under conditions as close as possible..