Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 240 MPa | >= 34800 psi | |
MetalTek HAYNES® HR120 Severe Corrosion and Heat Resistant Alloy Information provided by MetalTek |
|||
Tensile Strength, Yield | >= 240 MPa | >= 34800 psi | |
MetalTek MTEK 230-N Cast UNS C95800 Aluminum Bronze Versatile alloy with high strength, good ductility, unusual toughness, plus exceptional wear resistance. Aluminum Bronze heat treated to higher mechanical properties where necessary.Information prov.. |
|||
Tensile Strength, Yield | >= 240 MPa | >= 34800 psi | |
MetalTek MTEK WC 1 UNS J13047 Cast Alloy Steel General structural use.Applications: Cylinders, rolls, hollow shafts.Information provided by MetalTek |
|||
Tensile Strength, Yield | >= 240 MPa | >= 34800 psi | |
MetalTek MTEK 25-20 Cast UNS J94224 Heat Resistant Stainless Steel Increased strength for more highly stressed applications. Good resistance to oxidizing or reducing process flow.Applications: Calcining tubes, pier caps, high temperature fixtures and hardware.Infor.. |
|||
Tensile Strength, Yield | >= 240 MPa | >= 34800 psi | |
MetalTek MTEK 27-5 Cast UNS J93015 Heat Resistant Stainless Steel Higher nickel yields improved strength. Resists high sulfur process gas.Applications: Pour spouts, holding pots, kiln parts, gas parts.Information provided by MetalTek |
|||
Tensile Strength, Yield | >= 240 MPa | >= 34800 psi | |
MetalTek MTEK 28-48WCo Heat Resistant Stainless Steel Information provided by MetalTek |
|||
Tensile Strength, Yield | 240 MPa @Strain 0.200 %, Temperature 540 °C |
34800 psi @Strain 0.200 %, Temperature 1000 °F |
|
Haynes 556® alloy, cold rolled, solution annealed sheet, 0.8-2.8 mm thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Yield | 240 MPa @Strain 0.200 %, Temperature 650 °C |
34800 psi @Strain 0.200 %, Temperature 1200 °F |
Solution Annealed prior to test |
Special Metals NIMONIC® Alloy 86 A nickel-chromium-molybdenum alloy with a rare-earth (cerium) addition. It combines good formability and weldability with exceptional resistance to oxidation and scaling at temperatures to 1920°.. |
|||
Tensile Strength, Yield | 240 MPa | 34800 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP LC008E PEEK (Asia Pacific) LNP* Thermocomp* LC008E is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive. |
|||
Tensile Strength, Yield | 240 MPa | 34800 psi | |
AK Steel Hot Rolled Carbon Steel, Drawing Steel (DS Type B), Standard Grade DS is made by adding aluminum to the molten steel and may be used in drawing applications.Information provided by AK Steel |
|||
Tensile Strength, Yield | 240 MPa | 34800 psi | ISO 527-2 |
Ascend Performance Materials Vydyne® R550H Nylon 66, 50% Glass Reinforced, DAM Vydyne® R550H is general-purpose, heat-stabilized, hydrolysis-resistant, 50% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of physic.. |
|||
Tensile Strength, Yield | >= 240 MPa | >= 34800 psi | ASTM A240 |
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel-Molybdenum 317LXN™ (UNS S31726) Allegheny Ludlum's 317LXN™ is molybdenum-bearing austenitic stainless steel with greatly increased resistance to chemical attack as compared to the conventional chromium-nickel austenitic stainless.. |
|||
Tensile Strength, Yield | 240 MPa | 34800 psi | As Cast |
AFE Technologies Cronite 37Ni/18Cr No. HR5 High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF.. |
|||
Tensile Strength, Yield | 240 MPa @Strain 0.200 % |
34800 psi @Strain 0.200 % |
|
Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Yield | 240 MPa @Temperature 870 °C |
34800 psi @Temperature 1600 °F |
|
Haynes Hastelloy® alloy 625 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |