- Polymer Property : Tensile Strength, Yield = 34.3 MPa
Polymer Property : Tensile Strength, Yield = 34.3 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | ASTM D638 |
| PolyMirae Moplen HP526N IPP/WQBF Grade Polypropylene Moplen HP526N is the polypropylene homopolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen HP526N is a homopolymer particularly suitable for WQB (Water Quench.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | ASTM D638 |
| PolyMirae Moplen HP602N Injection Molding Grade Polypropylene Moplen HP602N is the polypropylene homopolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen HP602N is a homopolymer particularly suitable for injection molding.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | ASTM D638 |
| Hyosung Topilene F300 PP F300 Film Grade HomopolymerApplications: OPPCharacteristics:ProcessabilityTransparencyInformation provided by Hyosung Corporation |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | ASTM D638 |
| Hyosung Topilene S905H PP S905H Fiber Grade HomopolymerApplications: SpunboundCharacteristics:High flowabilityProcessabilityInformation provided by Hyosung Corporation |
|||
| Tensile Strength, Yield | 34.3 MPa @Thickness 3.20 mm |
4980 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| LG Chemical ALPHALAC SG910 HIPS High gloss and high impact equivalent to ABS, Excellent mechanical properties compare with general HIPS, Meet requirements for cost and quality, Applications include housing of electric appliancesCA.. |
|||
| Tensile Strength, Yield | 34.3 MPa @Thickness 3.20 mm |
4980 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| LG Chemical HIPS MI770 PS, Impact Modified Description: Injection Molding, PS, Impact Modified, High GlossApplication: Electric/Electronic Components, Stationary Articles, Food Containers, etc.CAS: 9003-55-8Information provided by LG Chemica.. |
|||
| Tensile Strength, Yield | 34.3 MPa @Thickness 3.20 mm |
4980 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| LG Chemical LUPOL GP3300 PP+MF30% Description: Injection Molding, PP+MF30%, General PurposeApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0 and 14807-96-6Information provided by LG Chemical |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | ASTM D638 |
| Global B-8200 High Density Polyethylene Description-high molecular weight, excellent stress cracking resistance,
excellent impact strength to blow moldApplications-large drums, gasoline tanks, agricultural chemical tanksInformation provi.. |
|||
| Tensile Strength, Yield | 34.3 MPa @Temperature 23.0 °C |
4970 psi @Temperature 73.4 °F |
ASTM D638 |
| Ineos H04G-00 Polypropylene Homopolymer This is a controlled rheology general purpose homopolymer polypropylene. This grade is designed to meet the processing and physical property requirements of film and profile extrusion applications... |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | 50mm/min; ASTM D638 |
| LG Chemical SEETEC H1500 Polypropylene Homopolymer Features: SEETEC H1500 is a high flow homopolymer suitable for injection molding applications. SEETEC H1500 exhibits a high flowability combined with a good mechanical property balance. SEETEC H1500.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | 50mm/min; ASTM D638 |
| LG Chemical SEETEC H5300 Polypropylene, Homopolymer Features: Seetec H5300 is designed for the extrusion of textile yarn and monofilaments. This grade is characterized by good processability and stretchability. SEETEC H5300 meets the FDA requirement .. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | 50mm/min; ASTM D638 |
| LG Chemical SEETEC H7411 Polypropylene, Homopolymer Features: Seetec H7411 is designed for the extrusion of continuous filament (CF) and staple fibers. This grade is characterized by high tenacity from narrow molecular weight distribution (MWD) and U.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | 50mm/min; ASTM D638 |
| LG Chemical SEETEC H7500 Polypropylene, Homopolymer Features: Seetec H7500 is designed for the extrusion of continuous filament (CF). This grade is characterized by medium MWD and good processability from specific additives. SEETEC H7500 meets the FD.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | 50mm/min; ASTM D638 |
| LG Chemical SEETEC H7511 Polypropylene, Homopolymer Features: Seetec H7511 is designed for the extrusion of staple fibers. This grade is characterized by high tenacity from narrow molecular weight distribution (MWD) and UV stability. SEETEC H7511 mee.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | 50mm/min; ASTM D638 |
| LG Chemical SEETEC H7525 Polypropylene, Homopolymer Features: Seetec H7525 is designed for the extrusion of staple fibers. This grade is characterized by Medium MWD and good thermobonding, with anti-gas fading stabilization. SEETEC H7525 meets the FD.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | 50mm/min; ASTM D638 |
| LG Chemical SEETEC H7700 Polypropylene, Homopolymer Features: Seetec H7700 is designed for the extrusion of fine fibers with the spunbond technology. This grade is characterized by very narrow molecular weight distribution (MWD), with anti-gas fading.. |
|||
| Tensile Strength, Yield | 34.3 MPa @Thickness 3.20 mm |
4980 psi @Thickness 0.126 in |
50 mm/min; ASTM D638 |
| LG Chemical SH625 ABS, High Impact, High Flow Feature: Extrusion Molding, High Impact, High FlowApplication: Ski Flat, MiscellaneousCAS No. 9003-56-9Information provided by LG Chemical |
|||
| Tensile Strength, Yield | 34.3 MPa | 4970 psi | ASTM D638 |
| Lotte Chemical Titan TITANPRO® PM383 Polypropylene homopolymer The base resin meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520(a)(1)(i) and (c)1.1a. The adjuvants meet their respective FDA regulations and 21 CFR 1.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4970 psi | ASTM D638 |
| Lotte Chemical Titan TITANPRO® PM803 Polypropylene homopolymer Titanpro® PM803 is a high flow and also a controlled rheology grade. The base resin meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520(a)(1)(i) and (.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Starex® SD-0190H ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Starex® SD-0190H ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | 9.8 in/min; ASTM D638 |
| Teknor Apex Sinvicomp SIC 3704 Polyvinyl Chloride, Rigid Notes: RoHS Compliant Availability: Asia Pacific Features: Medium Impact ResistanceUses: Rigid Packing; Tubing Forms: Pellets Processing Method: ExtrusionInformation Provided by Teknor Apex |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | ASTM D638 |
| SCG Chemicals EL-Leneâ„¢ H5840B High Density Polyethylene Blow Molding Key Characteristics:Excellent environmental stress cracking resistance (ESCR)Excellent appearanceOdorlessSafe for food contactGood printabilityRecommended Applications: Bottles for food, juice, sof.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4970 psi | 82% Ret. |
| UBE UBESTA® 3030U Nylon 12 (After Fuel C for 1000 hours) Description: UBESTA has a strong resistance to chemicals. Under normal conditions, it is not significantly affected by alkalis, alcohols, ethers, ketones, hydrocarbons, lubricating oils, gasoline, c.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4970 psi | ASTM D638 |
| Westlake Plastics Propylux® 290 Polypropylene, Heat Stabilized Through process improvement and advanced engineering, Westlake Plastics introduces the next generation of heat-stabilized polypropylene. Propylux 290 is produced from a FDA approved homopolymer res.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4970 psi | ASTM D638 |
| Westlake Plastics Propylux® HS2 Polypropylene for Medical Applications, Heat Stabilized Through process improvement and advanced engineering, Westlake Plastics introduces the next generation of heat-stabilized polypropylene. Propylux HS2 is produced from a FDA and USP Class VI approve.. |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | ASTM D638 |
| Cheng Yu Plastic PE221 Flame Retardant LDPE |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | ASTM D638 |
| Cheng Yu Plastic PP226 Flame Retardant Polypropylene, Medium Impact |
|||
| Tensile Strength, Yield | 34.3 MPa | 4980 psi | ASTM D638 |
| SCG Chemicals EL-Lene™ H6140B High Density Polyethylene Blow Molding Key Characteristics:Good processabilityHigh stiffnessGood environmental stress cracking resistance (ESCR)High compressive and impact strengthExcellent appearanceOdorlessSafe for food contactGood pri.. |
|||
| Tensile Strength, Yield | 34.3 MPa @Thickness 3.20 mm |
4980 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| LG Chemical LUPOL GP3100 PP+MF10% Description: Injection Molding, PP+MF30%, General PurposeApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0 and 14807-96-6Information provided by LG Chemical |
|||