Polymer Property : Tensile Strength, Yield = 3270 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 22.6 MPa

@Thickness 2.00 mm
3270 psi

@Thickness 0.0787 in
50mm/min; ASTM D638
LG Chemical KEYFLEX BT 1068D Ester Type TPE
Description: Injection Molding, TPC-ET, General Purpose, High ModulusApplication: Injection Parts for Automotives, Leisure & SportsCAS: 37282-12-5Information provided by LG Chemical
Tensile Strength, Yield 22.6 MPa
3270 psi
ASTM D638
Global F-8000 High Density Polyethylene
Description-good mechanical strengthApplications-blown wide film applications producing liner film & industrial filmInformation provided by Global Polymers Corporation.
Tensile Strength, Yield 22.6 MPa
3270 psi
ASTM D638
Global MB-6366 High Density Polyethylene
Description-high density for high quality, excellent creep & chemical resistanceApplications-drinking water pipe, industrial pipe, sewer pipeInformation provided by Global Polymers Corporation.
Tensile Strength, Yield 22.6 MPa
3270 psi
50mm/min; ASTM D638
LG Chemical SEETEC T3410 Polypropylene Random Terpolymer
Features: Seetec T3410 is a polypropylene-ethylene-butene random terpolymer designed for the production of Transparent Film and Expandable PP for low seal temperature and high impact strength. It of..
Tensile Strength, Yield 22.6 MPa
3270 psi
20 mm/min; ASTM D638
Samsung Cheil Industries Starex® VE-1801 HIPS, Unreinforced FR
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 22.6 MPa
3270 psi
20 mm/min; ASTM D638
Samsung Cheil Industries Starex® VE-1805 HIPS, Unreinforced FR
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 22.6 MPa
3270 psi
20 mm/min; ASTM D638
Samsung Cheil Industries Starex® VE-1801 HIPS, Unreinforced FR
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 22.6 MPa
3270 psi
20 mm/min; ASTM D638
Samsung Cheil Industries Starex® VE-1805 HIPS, Unreinforced FR
Information provided by Samsung Cheil Industries.
Tensile Strength, Yield 22.6 MPa
3270 psi
ASTM D638
SCG Chemicals EL-Leneâ„¢ H511W High Density Polyethylene Wire & Cable Grade
Key Characteristics: Contains special metal deactivator, high mechanical properties, high speed extrusionRecommended Applications: Insulation of communication cablesInformation provided by SCG Che..
Tensile Strength, Yield >= 22.5 MPa
>= 3270 psi
2 in/min; ASTM D638
A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene
DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman.
Tensile Strength, Yield >= 22.5 MPa
>= 3270 psi
2 in/min; ASTM D638
A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene
DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman.
Tensile Strength, Yield >= 22.5 MPa
>= 3270 psi
2 in/min; ASTM D638
A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene
DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman.
Tensile Strength, Yield >= 22.5 MPa
>= 3270 psi
2 in/min; ASTM D638
A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene
DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman.
Tensile Strength, Yield 22.6 MPa
3270 psi
Zylog Hipolyene® 7151 M1 HF Thermoplastic Polyolefin & PP Compound
Information provided by Zylog Plastalloys Pvt. Ltd.
Tensile Strength, Yield >= 22.5 MPa
>= 3270 psi
2 in/min; ASTM D638
A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene
DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman.
Tensile Strength, Yield 22.6 MPa
3270 psi
Zylog Hipolyene® 1532 HC EX Thermoplastic Polyolefin & PP Compound
Information provided by Zylog Plastalloys Pvt. Ltd.
Tensile Strength, Yield 22.6 MPa
3270 psi
ASTM D638
Total Lacqrene® 814(AS) High Impact Polystyrene  (discontinued **)
LACQRENE® 814 is a high impact, flame retardant polystyrene, free from PBDPE and with excellent thermal stability.ApplicationCovers for electrical equipment, Office equipment: copiers, faxInformati..
Tensile Strength, Yield >= 22.5 MPa
>= 3270 psi
2 in/min; ASTM D638
A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene
DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman.
Tensile Strength, Yield 22.6 MPa
3270 psi
ASTM D638M
Total Lacqrene® 4431 Flame Retardant Polystyrene  (discontinued **)
LACQRENE ® 4240 is a high impact, flame retardant polystyrene with excellent thermal stability.ApplicationTelevision back coversInformation provided provided by Total Petrochemicals.Total Petrochem..