Polymer Property : Tensile Strength, Yield = 300 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 300 MPa

@Strain 0.200 %,
Temperature 315 °C
43500 psi

@Strain 0.200 %,
Temperature 599 °F
Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet
The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Tensile Strength, Yield <= 300 MPa

@Strain 0.200 %,
Thickness <=0.700 mm
<= 43500 psi

@Strain 0.200 %,
Thickness <=0.0276 in
20 MPa higher apply
SSAB Tunnplat Aluzink F26A Metal-coated Mild Steel
Metal-coated Mild SteelComments: Aluzink - Aluminum-zinc coated sheet. Property values are for thicknesses 0.4 - 2.00 mm. Iron content is approximate - exact composition is not reported by the manu..
Tensile Strength, Yield 300 - 360 MPa

@Strain 0.200 %
43500 - 52200 psi

@Strain 0.200 %
SSAB Tunnplat Docol® 300 RP High-strength Steel
High-strength SteelComments: Docol RP - Cold Rolled Steel - rephosphorized steel. Property values are for cold-rolled steel; thicknesses 0.40 - 3.0 mm. Iron content is approximate - exact compositi..
Tensile Strength, Yield 300 - 390 MPa

@Strain 0.200 %
43500 - 56600 psi

@Strain 0.200 %
SSAB Tunnplat Docol® 500DP High-strength Steel
High-strength SteelComments: Docol DP - Cold Rolled Steel - dual-phase steel. Property values are for cold-rolled steel; thicknesses 0.5 - 1.6 mm. Iron content is approximate - exact composition is..
Tensile Strength, Yield <= 300 MPa

@Strain 0.200 %
<= 43500 psi

@Strain 0.200 %
SSAB Tunnplat Dogal F26 Metal-coated Mild Steel
Metal-coated Mild SteelComments: Dogal - Hotdipped-galvanized sheet. Property values are for thicknesses 0.5 - 2.5 mm. Iron content is approximate - exact composition is not reported by the manufac..
Tensile Strength, Yield 300 MPa

@Temperature 100 °C
43500 psi

@Temperature 212 °F
90º, Wet; EN2561
Hexcel® HexPly® M12 135°C Curing Epoxy Matrix, 37%/7781 Fiber
Information provided by HexCel
Tensile Strength, Yield <= 300 MPa

@Strain 0.200 %
<= 43500 psi

@Strain 0.200 %
CLAL-MSX ARCAP Anticorrosion AP1 0 Annealed, Rolled Copper Alloy
Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin..
Tensile Strength, Yield >= 300 MPa

@Strain 0.200 %
>= 43500 psi

@Strain 0.200 %
CLAL-MSX CUPROROR® TL2 1/2 hard, Copper Alloy
Alloy especially suited to applications in electronics and electro technology. This doped copper, displays high electrical and thermal conductivity, good mechanical properties and excellent temperat..
Tensile Strength, Yield >= 300 MPa

@Strain 0.200 %
>= 43500 psi

@Strain 0.200 %
CLAL-MSX NICLAFOR® 1000 TD1 Quenched/Cold Rolled, Drawn Copper Alloy
Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Yield >= 300 MPa

@Strain 0.200 %
>= 43500 psi

@Strain 0.200 %
CLAL-MSX NICLAFOR® 1000 TD1 Quenched/Cold Rolled, Rolled Copper Alloy
Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Yield >= 300 MPa

@Strain 0.200 %
>= 43500 psi

@Strain 0.200 %
CLAL-MSX ARCAP Anticorrosion AP1 H11 1/4 hard, Rolled Copper Alloy
Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin..
Tensile Strength, Yield <= 300 MPa

@Strain 0.200 %
<= 43500 psi

@Strain 0.200 %
CLAL-MSX ARCAP Anticorrosion AP1C 0 Annealed, Rolled Copper Alloy
Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un..
Tensile Strength, Yield >= 300 MPa

@Strain 0.200 %
>= 43500 psi

@Strain 0.200 %
CLAL-MSX ARCAP Anticorrosion AP1C H11 1/4 hard, Rolled Copper Alloy
Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un..
Tensile Strength, Yield <= 300 MPa

@Strain 0.200 %
<= 43500 psi

@Strain 0.200 %
CLAL-MSX ARCAP Anticorrosion AP4 0 Annealed, Rolled Copper Alloy
Description: The AP4 grade is less easy to turn than the other grades of ARCAP. It can however be machined without more difficulty than the nickel chromium molybdenum steels.High Corrosion Resistanc..
Tensile Strength, Yield >= 300 MPa

@Strain 0.200 %
>= 43500 psi

@Strain 0.200 %
CLAL-MSX ARCAP Anticorrosion AP4 H11 1/4 hard, Rolled Copper Alloy
Description: The AP4 grade is less easy to turn than the other grades of ARCAP. It can however be machined without more difficulty than the nickel chromium molybdenum steels.High Corrosion Resistanc..
Tensile Strength, Yield 300 - 380 MPa
43500 - 55100 psi
ArcelorMittal Dual Phase 500 Very high strength steel, Cold Rolled Steel
Available in the following: HCT600X (uncoated), HCT600X+ZE (electrogalvanized) and HCT600X+Z/ZF (Extragal®/Galvannealed)Description: Dual Phase steels offer an outstanding combination of strength a..
Tensile Strength, Yield 300 - 340 MPa
43500 - 49300 psi
ArcelorMittal IF 300 High strength IF steel, Cold rolled
Available in the following: Extragal®/Galvannealed (HX300YD+Z/+ZF)Description: These steels were designed to provide an excellent combination of drawability and mechanical strength based on their ..
Tensile Strength, Yield 300 - 360 MPa
43500 - 52200 psi
ArcelorMittal 300 BH Bake hardening steel, Cold rolled
Available in the following: uncoated (HC300B), electroglavanized (HC300B+ZE) and Extragal®/Galvannealed (HC300BD+Z)Description: The composition and processing of these steels are designed to promot..
Tensile Strength, Yield 300 - 380 MPa
43500 - 55100 psi
ArcelorMittal FB 450 Hot rolled ferrite-bainite steel
Available in the following: uncoated (HDT450F) and Extragal® (HDT450F+Z)Description: This range of hot-rolled high strength steels has been developed to meet weight reduction requirements. It compr..
Tensile Strength, Yield 300 - 380 MPa
43500 - 55100 psi
ArcelorMittal FF 280 D Very high strength steel, Cold Rolled Steel
Available in the following: HCT450X (uncoated), HCT450X+ZE (electrogalvanized) and HCT450X+Z/ZF (Extragal®/Galvannealed)Description: Dual Phase steels offer an outstanding combination of strength a..
Tensile Strength, Yield 300 - 360 MPa
43500 - 52200 psi
ArcelorMittal H 360 Solid solution steel, Cold rolled
Available in the following: uncoated (HC300P) and electrogalvanized (HC300P+ZE) Description: Solid solution steels are designed to provide high strength while maintaining good drawability. These ste..
Tensile Strength, Yield 300 - 360 MPa
43500 - 52200 psi
ArcelorMittal HSLA 300 High strength low alloy steel for cold forming, Cold Rolled
Available in the following: uncoated (HC300LA), electroglavanized (HC300LA +ZE) and Extragal®/galfan/Galvannealed (HC300LA+Z/+ZA/+ZF)Description: Steels in the HSLA (High Strength Low Alloy) range ..
Tensile Strength, Yield 300 MPa
43500 psi
typical
ATI Allegheny Ludlum AL 825™ Nickel Alloy
Allegheny Ludlum AL 825 alloy is an austenitic nickel-iron-chromium-molybdenum-copper alloy containing high levels of corrosion resistance to both moderately oxidizing and moderately reducing enviro..
Tensile Strength, Yield 300 MPa

@Strain 0.200 %
43500 psi

@Strain 0.200 %
Annealed prior to test
Special Metals INCOLOY® Alloy 020
A nickel-iron-chromium alloy with additions of copper and molybdenum. It also contains niobium for stabilization against sensitization and resultant intergranular corrosion. The alloy has excellen..