Polymer Property : Tensile Strength, Yield = 26300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 181 MPa
26300 psi
ASTM D638
LNP Thermocomp® UF-1006 FR HS LEX BK8-115 Polyphthalamide, Glass Fiber Reinforcement  (discontinued **)
Features: Heat Stabilized, Flame RetardantForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many L..
Tensile Strength, Yield 181 MPa
26300 psi
ASTM D638
LNP Thermocomp® LF-1006 EM Polyetheretherketone, Glass Fiber Reinforcement  (discontinued **)
Features: Good MoldabilityForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are st..
Tensile Strength, Yield 181 MPa
26300 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP QF00A PA6.10
LNP* THERMOCOMP* QF00A is a compound based on Nylon 6/10 containing 50% Glass Fiber.
Tensile Strength, Yield 181 MPa
26300 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP QF00A PA6.10
LNP* THERMOCOMP* QF00A is a compound based on Nylon 6/10 containing 50% Glass Fiber.
Tensile Strength, Yield 181 MPa

@Strain 0.200 %,
Temperature 760 °C
26300 psi

@Strain 0.200 %,
Temperature 1400 °F
Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F)
Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac..