Polymer Property : Tensile Strength, Yield = 25400 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 175 MPa
25400 psi
ASTM D638
NYCOA 27/300SR Glass Filled Nylon 6
30% glass filled, flame retardant to UL 94 H-B nylon 6Information provided by NYCOA, Inc.
Tensile Strength, Yield 175 MPa
25400 psi
ISO 527-1/-2
Lanxess Durethan® DP 2037/30 H2.0 LT 904040 Nylon 6, 30% Glass Fiber
PA 6, 30% glass fibers, black colored for laser transmission-welding (laser-transparent), good heat-ageing resistance
Tensile Strength, Yield 175 MPa

@Strain 0.200 %,
Temperature 760 °C
25400 psi

@Strain 0.200 %,
Temperature 1400 °F
Haynes HR-120® alloy, solution heat-treated plate
Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Tensile Strength, Yield 175 MPa

@Strain 0.200 %,
Temperature 540 °C
25400 psi

@Strain 0.200 %,
Temperature 1000 °F
Haynes HR-120® alloy, solution heat-treated plate
Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Tensile Strength, Yield 175 MPa
25400 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP OCP36 PPS
LNP* LUBRICOMP* OCP36 is a compound based on Polyphenylene Sulfide resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Wear Resistant, Bearing Grade, Electr..
Tensile Strength, Yield 175 MPa
25400 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP OCP36 PPS
LNP* LUBRICOMP* OCP36 is a compound based on Polyphenylene Sulfide resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Wear Resistant, Bearing Grade, Electr..
Tensile Strength, Yield 175 MPa
25400 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON RX05489 PA 66
LNP* STAT-KON* RX05489 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 20% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear..
Tensile Strength, Yield 175 MPa
25400 psi
ISO 527
SABIC Innovative Plastics LNP Thermocomp EF008E PEI
LNP* Thermocomp* EF008E is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas..
Tensile Strength, Yield 175 MPa
25400 psi
ISO 527
SABIC Innovative Plastics LNP Thermocomp EF008E PEI (Asia Pacific)
LNP* Thermocomp* EF008E is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Asia Pac..
Tensile Strength, Yield 175 MPa
25400 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF006S PA6.6 (Europe-Africa-Middle East)
LNP* THERMOCOMP* RF006S is a compound based on PA 66 resin containing Glass Fiber. Added features include: Heat Stabilized.
Tensile Strength, Yield 175 MPa
25400 psi
5 mm/min; ISO 527
SABIC Innovative Plastics Valox® V8090 PBT+PET (Europe-Africa-Middle East)
50% Glass Fiber Reinforced PBT-PET resin
Tensile Strength, Yield >= 175 MPa

@Strain 0.200 %
>= 25400 psi

@Strain 0.200 %
Schmolz + Bickenbach UGICHROM 4307 Austenitic Chrome Plated Bar
Description: Ugichrom combines the high efficiency of micro-fissuring chromium plating with the technology of Ugitech’s most advanced gradesAdvantages: Zero defects guarantee; Low friction coef..
Tensile Strength, Yield 175 MPa
25400 psi
ISO 527
Polyram PlusTek PA303G6BK16 Nylon 6.6, 30% Glass Fiber reinforced, Heat Stabilized, Hydrolysis Resistant
30% Glass fiber reinforced, heat stabilized, hydrolysis resistant, improved surface finish Nylon 6.6. Approved and listed by W.R.A.S.Information provided by Polyram.
Tensile Strength, Yield 175 MPa
25400 psi
ASTM-D638
Polyram PlusTek PA309G6 Nylon 6.6, 30% Glass Fiber
30% glass fiber reinforced, UV stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Tensile Strength, Yield 175 MPa
25400 psi
ASTM-D638
Polyram PlusTek PA4801G6 Nylon 6.6, 30% Glass Fiber Reinforced, PTFE lubricated
30% glass fiber reinforced, PTFE lubricated polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Tensile Strength, Yield 175 MPa
25400 psi
ASTM D638
Solvay TECHNYL® 1021GF6 PA6, 30% glass fiber, DRY
Description: Polyamide 6, 30% glass fiber reinforced, for injection molding.Available in: Asia Pacific Product Applications: TECHNYL® 1021GF6 is used in all sectors of industry, offering an excelle..