Polymer Property : Tensile Strength, Yield = 25.2 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	25.2 MPa	3650 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable EHA70L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield	25.2 MPa	3650 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Wire & Cable W3200 Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne
Tensile Strength, Yield	25.2 MPa	3650 psi	2 in per min; ASTM D638
Network Polymers NPP 25-5001 Description: Copolymer PolypropyleneInformation provided by Network Polymers Inc.
Tensile Strength, Yield	25.2 MPa	3650 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N650 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	25.2 MPa	3650 psi	aged in air at 100ºC for 4 days
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with No Plasticizer MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	25.2 MPa	3650 psi	ASTM D638
M. Holland Company CP200 Polypropylene Impact Copolymer Impact copolymerMedium impact resistanceLow temperature impact resistanceApplications: Appliance componentsConsumer ApplicationsHousehold goodsInformation provided by M. Holland
Tensile Strength, Yield	25.2 MPa	3650 psi	2 in/min; ASTM D638
A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used..
Tensile Strength, Yield	25.2 MPa	3650 psi	2 in/min; ASTM D638
A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	25.2 MPa	3650 psi	2 in/min; ASTM D638
A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used..
Tensile Strength, Yield	25.2 MPa	3650 psi	2 in/min; ASTM D638
A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	25.2 MPa	3650 psi	2" (50mm) per min; ASTM D638
Formosa Plastics Formolene® 6600A Impact Copolymer Polypropylene Impact Copolymer for Extrusion and Compounding Applications (Fractional Melt Flow) Formolene® 6600A is a high impact copolymer with an excellent balance of toughness and stiffness. It is suitable f..
Tensile Strength, Yield	25.2 MPa	3650 psi	2 in/min; ASTM D638
A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used..
Tensile Strength, Yield	25.2 MPa	3650 psi	2 in/min; ASTM D638
A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	25.2 MPa	3650 psi	2 in/min; ASTM D638
A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	25.2 MPa	3650 psi	2 in/min; ASTM D638
A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman.
Tensile Strength, Yield	25.2 MPa	3660 psi
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Tensile Strength, Yield	25.2 MPa	3650 psi	aged in air at 100ºC for 4 days
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with No Plasticizer MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	25.2 MPa	3650 psi	aged in air at 100ºC for 4 days
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with TCP Plasticizer MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	25.2 MPa	3650 psi	2 in/min; ASTM D638
A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used..
Tensile Strength, Yield	25.2 MPa	3650 psi	2" (50mm) per min.; ASTM D638
Formosa Plastics Formolene® 6510A Injection Molding Polypropylene Impact CopolymerApplications: Closures, Housewares, Small Appliance, Battery Cases and LidsFormolene 6510A is a medium impact copolymer of polypropylene characterized by its easy mold flow, physical..
Tensile Strength, Yield	25.2 MPa	3660 psi
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Tensile Strength, Yield	25.2 MPa	3650 psi
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 84A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Tensile Strength, Yield	25.2 MPa	3650 psi
TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, 30.0 PHR Wacker HDK N20 Filler Millathane 97 is a polyether polyurethane rubber having excellent transparency, good wear properties, a high coefficient of friction and very good UV stability. This polyurethane rubber is designed ..
Tensile Strength, Yield	25.2 MPa	3650 psi	2 in/min; ASTM D638
A. Schulman SUPERLINEAR™ XL 0360 Rotational Molding Resin DescriptionSuperlinear XL 0360 is compounded rotational molding resin based on metallocean catalyst technology. This technology allows for high impact and excellent stiffness. It is typically used..
Tensile Strength, Yield	25.2 MPa	3650 psi	ASTM D-638
Axiall 8621 Moldings & Extrusions Flexible PVC High quality, semi-rigid extrusion compound especially formulated for extruded T-moldings and other shapes where uniform flow through the die is required.Information provided by Georgia GulfGeorgia ..
Tensile Strength, Yield	25.2 MPa	3660 psi
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Tensile Strength, Yield	25.2 MPa	3660 psi
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c..
Tensile Strength, Yield	25.2 MPa	3650 psi
TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, 30.0 PHR Wacker HDK N20 Filler Millathane 97 is a polyether polyurethane rubber having excellent transparency, good wear properties, a high coefficient of friction and very good UV stability. This polyurethane rubber is designed ..
Tensile Strength, Yield	25.2 MPa	3650 psi	aged in air at 100ºC for 4 days
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with TCP Plasticizer MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	25.2 MPa	3650 psi	2 in/min; ASTM D638
A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1247 is a 25% mineral filled copolymer polypropylene.Information provided by A. Schulman.