Polymer Property : Tensile Strength, Yield = 23100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 159 MPa
23100 psi
5.1 mm/min; ASTM D638
PolyOne LubriOne™ SF-30CF/15T Polyphenylene Sulfide (PPS)
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Tensile Strength, Yield 159 MPa
23100 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP 9X98026 PA 46 (Europe-Africa-Middle East)
LNP* Lubricomp* 9X98026 is a compound based on PA4.6 resin containing Barium Sulfate, PTFE and Carbon Fiber
Tensile Strength, Yield 159 MPa
23100 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp RF006PS PA 66
LNP* Thermocomp* RF-1006 EP HS is based on Nylon 6/6 containing Glass Fiber. Characteristics of this grade include Exceptional Processing and Heat Stabilizer.This data was supplied by SABIC-IP for ..
Tensile Strength, Yield 159 MPa
23100 psi
.0275 - .035 inches sheet thickness; ASTM A 370
AK Steel ASTM A 424 Type III, I-F Enamel Enameling Carbon Steel
I-F Enameling Steel is a vacuum degassed, titanium stabilized steel. I-F Enameling Steel can be used for ground coat and two coat-one fire porcelain enameling systems. It is not recommended for us..
Tensile Strength, Yield 159 MPa
23100 psi
AK Steel Cold Rolled Carbon Steel, Extra Deep Drawing Steel (EDDS), Standard Grade
Interstitial Free (I-F) steels are made by adding titanium and/or niobium to the molten steel after vacuum degassing and offer excellent drawability.Information provided by AK Steel
Tensile Strength, Yield 159 MPa
23100 psi
.0275 - .035 inches sheet thickness; ASTM A 370
AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, Extra Deep Drawing Steel Plus (EDDS+), Standard Grade
Interstitial Free (I-F®) steels are made by adding titanium and/or columbium to the molten steel after vacuum degassing and offer excellent drawability.Information provided by AK Steel
Tensile Strength, Yield 159 MPa
23100 psi
ASTM D638
Ashley Polymers Ashlene® 830L-25G Nylon 6, 25% Glass Reinforced
A 25% glass fiber reinforced Nylon 6 designed to provide a high flexural modulus and good dimensional stability while maintaining the ease of processing associated with Nylon 6 type material.Data pr..